    摘要 二氧化锆(ZrO2)气凝胶有望兼具 ZrO2优异热学稳定性、化学稳定性及催化性能和气凝胶高比表面积、高空隙率特性,拥有诱人的潜在性质和应用前景,可用作催化剂载体、超级隔热材料等。传统制备 ZrO2气凝胶方法都是采用超临界干燥,而且大多以锆的金属醇盐为前驱体,成本高,安全性差。发展价格便宜的无机盐前驱体以及常压干燥技术己成为ZrO2气凝胶材料研究及应用的重要方向。本文在综合论述气凝胶及 ZrO2气凝胶的基础上,分别以以硝酸氧锆ZrO(NO3)2•3H2O、氧氯化锆(ZrOCl2•8H2O)和四氯化锆(ZrCl4)三种无机锆盐为前驱体进行 ZrO2气凝胶的常压干燥制备,其中选择气凝胶特性较好的四氯化锆前驱体,深入研究了四氯化锆前驱体体系中环氧丙烷量、醇-水比、锆盐浓度、干燥温度等各工艺要素对ZrO2气凝胶结构与性能的影响。由XRD衍射仪、SEM 电子显微镜、热重分析对气凝胶进行表征,测试结果表明使用四氯化锆(ZrCl4)无机盐、醇-水体积比3:1、干燥温度控制在 60℃等工艺条件下能够实现 ZrO2气凝胶常压干燥的目的。  35876
    毕业论文关键词:气凝胶  氧化锆  常压干燥  溶胶-凝胶法      
    Abstract Combining catalytic activity, good thermal and chemical stabilities of zirconia (ZrO2)with high  surface  area and high porosity of aerogels,  zirconia  aerogels have  various  potential applications such as catalyst supporting materials, super heat insulation materials. However, the traditional drying method to prepare  ZrO2  aerogels  is supercritical drying with  zirconium alkoxide as precursor,  which is expensive and  dangerous.It is necessary to develop  ZrO2 aerogels by using inorganic salt as  precursor and ambient pressure drying.In this  paper, zirconyl nitrate(ZrO(NO3)2• 3H2O), zirconyl chloride octahydrate (ZrOCl2• 8H2O)and zirconium (Iv) chloride(ZrCl4)were used as inorganic salt precursor to synthesize ZrO2 aerogels through ambient pressure drying.Select airgel characteristics of a good precursor of zirconium tetrachloride, zirconium tetrachloride-depth study of the precursor system in the amount of propylene oxide, alcohol - water ratio of various process elements, zirconium salt concentration, drying temperature on ZrO2 aerogels effect of structure and properties of rubber. By the XRD diffraction, SEM electron microscopy, TGA aerogels were characterized test results show that the use of zirconium tetrachloride (ZrCl4) inorganic salt, alcohol  - water volume ratio of 3: 1, and dried at 60  ℃  temperature control and other process ZrO2 airgel can be achieved under the conditions of atmospheric drying purposes. 
    Key Words:Aerogel;Zirconia;Ambient pressure drying;Sol-gel
    目录
    1绪论.1
    1.1气凝胶材料..1
    1.2ZrO2材料...2
    1.3ZrO2气凝胶材料.3
    1.4ZrO2气凝胶制备方法简介.3
    1.4.1沉淀法..3
    1.4.2锆醇盐水解法4
    1.4.3醇-水加热法.4
    1.4.4滴加环氧丙烷法..4
    1.5溶胶-凝胶法.4
    1.6超临界干燥与常压干燥6
    1.6.1超临界干燥..6
    1.6.2常压干燥6
    1.7选题的目的和研究内容7
    1.7.1选题背景7
    1.7.2研究内容8
    2实验部分.9
    2.1实验原料及实验仪器和设备9
    2.1.1实验原料9
    2.1.2实验仪器及设备..9
    2.2主要仪器设备简介...10
    2.2.1XRD衍射仪10
    2.2.2SEM电子显微镜10
    2.2.3热重分析仪.11
    2.3实验过程...11
    2.3.1ZrO2湿凝胶的制备..11
    2.3.2ZrO2湿凝胶的陈化与干燥12
    3实验结果分析13
    3.1不同无机盐选择对ZrO2气凝胶凝胶的影响..13
    3.2不同原料配比常压制备ZrO2气凝胶的研究..15
    3.2.1不同环氧丙烷添加量对ZrO2气凝胶的影响..15
  1. 上一篇:过量掺杂原位共生法制备多铁性复合材料
  2. 下一篇:水热法合成无稀土永磁材料的研究
  1. 基于近常压光电子能谱的...

  2. 巴金《激流三部曲》高觉新的悲剧命运

  3. 现代简约美式风格在室内家装中的运用

  4. 浅析中国古代宗法制度

  5. g-C3N4光催化剂的制备和光催化性能研究

  6. NFC协议物理层的软件实现+文献综述

  7. 中国传统元素在游戏角色...

  8. C++最短路径算法研究和程序设计

  9. 高警觉工作人群的元情绪...

  10. 江苏省某高中学生体质现状的调查研究

  11. 上市公司股权结构对经营绩效的影响研究

  

About

优尔论文网手机版...

主页:http://www.youerw.com

关闭返回