摘要:异步轧制是因上下工作辊的圆周速度不同,而使轧制变形区产生一种搓轧变形的轧制技术,异步轧制属于一种超细晶材料制备技术。TWIP钢的高强韧性来自形变过程中孪晶的形成,因此将该钢命名为孪生诱发塑性( twinning induced plasticity,TWIP)钢,其优良的综合性能使其在未来高强度高塑钢铁市场中处于非常优势的地位。本文利用二辊异步实验轧机分别对TWIP钢进行了同步轧制与异步轧制(SR=1.5),并对轧制试样在600℃~900℃范围内进行了退火试验。利用金相显微镜,硬度测试仪等设备,对TWIP钢进行组织性能测试。结果表明:同等状态下的异步轧制TWIP钢具有更高的硬度,两者的再结晶温度均介600℃~700℃之间,且异步轧制TWIP钢有着更低的再结晶温度。62081

毕业论文关键词:异步轧制;TWIP钢;组织;硬度;力学性能

Mechanical Properties and Microstructures of the TWIP Steels processed by asymmetric Rolling

Abstract:Asymmetric rolling is one type of rolling technology that makes the rolling deformation zone have a rubbing roll deformation ,due to the upper and lower work rolls have different circumferential speed ,it belongs a kind of preparation technology of ultrafine grained materials .TWIP steel has high strength and toughness because it produces a lot of  twins during deformation, so we call it twinning induced plasticity, its excellent comprehensive properties which is high strength and high plastic make it a very dominant position in the future steel market.In this article,using TWIP steel to carry out asymmetric rolling (SR=1.5) and symmetric rolling by two-high rolling mill,then ,carrying out annealing experiment in the range of 600℃~700℃ with the samples after being rolled .We can use some equipments to test its properties such as metallographic microscope , hardness tester and so on. The results show that we can get TWIP steel with higher hardness by asymmetric Rolling in the same condition,recrystallization temperature of both are between 600℃~700℃,and TWIP steel with asymmetric rolling has lower recrystallization temperature.

KeyWords:Asymmetric Rolling;TWIP Steel;Microstructure;hardness ;Mechanical properties

目 录

1 绪论 1

 1.1 异步轧制 1

  1.1.1 异步轧制的定义 1

  1.1.2 异步轧制的特点 1

  1.1.3 异步轧制工艺的发展 2

  1.1.4 异步轧制的优点和不足 3

  1.1.5 异步轧制的研究应用现状 3

 1.2 TWIP钢 3

  1.2.1 TWIP钢的成分分析 3

  1.2.2 TWIP钢的微观组织 4

  1.2.3 TWIP钢的优点 4

  1.2.4 TWIP钢的发展 5

  1.2.5 TWIP钢的研究现状 5

 1.3 课题研究的目的和意义 5

2 课题研究的内容和方法 6

 2.1 实验设备 6

  2.1.1 轧制设备 6

  2.1.2 其它实验设备 6

 2.2 实验方案 7

  2.2.1 实验流程 7

  2.2.2 轧制工艺的制定 7

 2.3 实验过程

上一篇:年产2000吨锌白铜板带车间工艺设计
下一篇:新型718合金高温氧化行为的研究

累积叠轧制备Al/Mg/Al叠层复...

三辊行星轧机轧制铝包铜...

三辊行星轧机轧制铝包铜...

AZ31镁合金异步轧制过程的DEFORM模拟研究

DEFORM纯铝板纵横交叉轧制过程的数值仿真研究

轧制态与挤压态6005A铝合金...

蛇形轧制过程的有限元模拟

我国风险投资的发展现状问题及对策分析

LiMn1-xFexPO4正极材料合成及充放电性能研究

安康汉江网讯

互联网教育”变革路径研究进展【7972字】

ASP.net+sqlserver企业设备管理系统设计与开发

老年2型糖尿病患者运动疗...

麦秸秆还田和沼液灌溉对...

网络语言“XX体”研究

新課改下小學语文洧效阅...

张洁小说《无字》中的女性意识