摘要：本论文主要研究了Q-T-P工艺对17-4PH不锈钢组织和力学性能的影响。首先将17-4PH不锈钢试样在1050°C下保温30min后进行淬火，接着进行回火-碳分配热处理。通过拉伸实验，显微维氏硬度测试研究了实验钢的力学性能；通过光学显微镜和扫描电镜观察了实验钢的显微组织。结果表明，经过Q-T-P工艺处理的组织，晶粒轮廓较清晰，回火马氏体仍然保留了板条状形貌，且位向关系明确。随着回火温度升高，晶粒尺寸增加，随着碳分配温度的升高，铁素体增多硬度和强度逐渐降低。74074

毕业论文关键词：17-4PH不锈钢；Q-T-P工艺；碳分配；金相组织

Study on Q - T - P Process of 17-4PH Stainless Steel

Summary：In this paper, the effect of Q-T-P process on the microstructure and mechanical properties of 17-4PH stainless steel was studied。 The 17-4PH stainless steel samples were first quenched at 1050 ° C for 30 min, followed by tempering-carbon distribution heat treatment。 The mechanical properties of the test steels were studied by tensile test and microscopic Vickers hardness test。 The microstructures of the experimental steels were observed by optical microscopy and scanning electron microscopy。 The results show that after the Q-T-P process, the grain profile is clearer, and the tempered martensite still retains the strip shape, and the orientation is clear。 As the tempering temperature increases, the grain size increases, and as the carbon distribution temperature increases, the ferrite increases hardness and strength gradually decreases。

KeyWords: 17-4PH stainless steel; Q-T-P process; carbon distribution; metallographic organization

目 录

1绪论 1

1。1不锈钢简介 1

1。1。1 不锈钢 1

1。1。2 不锈钢的分类 1

1。1。3  不锈钢概况 2

1。2 17-4PH不锈钢 4

1。2。1 17-4PH不锈钢简介 4

1。2。2 17-4PH不锈钢合金元素的作用 6

1。3 Q-T-P工艺 7

1。3。1 Q-T-P工艺的由来 7

1。4 选题的意义与目的 7

2 实验材料与方案 8

2。1 实验材料 8

2。2 实验方案制定 8

2。2。1 热处理方案的制定 8

2。2。2 回火-碳分配温度制定 8

2。3 实验方案实施 9

2。3。1 热处理 9

2。3。2 金相制样和观察 10

2。3。3 力学性能测试 11

2。3。4 扫描电镜观察材料 13

3 实验结果与分析 14

3。1 拉伸实验 14

3。2 金相组织分析 17

3。3试样扫描电镜观察实验 19

3。4 硬度测试分析 21

4 结论 23

致谢 24

参考文献 25

1绪论

1。1不锈钢简介

1。1。1 不锈钢