摘要：凹凸棒土是一种富含镁铝硅酸盐和水的黏土矿物，是一种天然的纳米矿物。我省淮安盱眙地区的凹凸棒土矿产资源非常丰富，且价格低廉。其所具备的独特纤维状或棒状晶体形态使其呈现出较好的吸附作用和较大的比表面积。为了提高凹凸棒土的吸附性能，本课题采用离子交换法，制备了用硝酸铜改性的凹凸棒土，在箱式电阻炉250℃下烘干5。5小时后，对凹凸棒土进行了XRD、BET、ICP表征。根据所设计的正交实验表，将改性凹凸棒土在25组不同条件下置于硫醇与甲醇混合溶液中吸附硫醇，用气相色谱仪检测吸附效果。实验结果表明，当硫醇浓度为1。2%，液土比为1，吸附时间为1 h时，改性凹凸棒土对硫醇的吸附效果最佳。85789

毕业论文关键词：凹凸棒土，铜离子，硫醇，吸附

Abstract：Attapulgite is a kind of clay mineral rich in magnesium aluminum silicate and water, and it is a kind of natural nano mineral。 The attapulgite mineral resources in Huaian area of Xuyi province are very rich and low in price。 It has a unique fibrous or rodlike crystal shape, showing good adsorption properties and larger specific surface area。 In order to improve the adsorption performance of attapulgite, using the ion exchange method, preparation of Attapulgite Modified by copper in the box type resistance furnace under 250℃ for 5。5 hours after drying, the attapulgite was XRD, BET, ICP。 According to the orthogonal experimental table designed, the modified attapulgite was adsorbed in the mixed solution of thiol and methanol under 25 different conditions, and the adsorption effect was detected by gas chromatograph。 The experimental results show that when the thiol concentration was 1。2%, liquid ratio is 1, the adsorption time is 1 h, the modified attapulgite adsorption effect of mercaptan best。

Keywords：Attapulgite , Copper ions, Mercaptan, Adsorption

目 录

1。  前言 4

1。1  凹凸棒土的物化性质 4

1。2  凹凸棒土的资源含量 5

1。3  硝酸铜的物化性质 5

1。4  硫醇的物化性质 6

1。5  油品中硫醇的脱除 6

1。6  课题意义 7

2。  实验过程 7

2。1  实验原料源Q于W优H尔J论K文M网WwW.youeRw.com 原文+QQ75201.,8766 、试剂及仪器 7

2。2  改性凹凸棒土的制备 8

2。2。1  凹凸棒土的酸洗 8

2。2。2  凹凸棒土的改性 9

2。3  改性凹凸棒土吸附硫醇 9

2。3。1  实验过程设计 9

2。3。2  甲醇硫醇溶液的配制 10

2。3。3  吸附效果的检测 10

3。  实验结果及讨论 11

3。1  实验样品表征及分析 11

3。1。1  XRD表征 11

3。1。2  BET表征 12

3。1。3  ICP表征 12

3。2  实验数据 13

3。2。1  实验数据处理及分析 14