摘要：本文用聚丙烯酸（PAA）改性凹凸棒土（PGS），并将其添加到聚偏氟乙烯（PVDF）铸膜液里共混制得复合超滤膜。考察不同改性凹土量对复合超滤膜纯水通量、BSA截留率、静态吸附等性能的影响。结果表明，改性凹土含量越大，膜的纯水通量越大、修正污染指数越小；当改性凹土相对量为7 wt。%时，膜对BSA的截留率最大，表明该膜的分离效果相对最好；室温下，当改性凹土相对量为1 wt。%时，改性膜对BSA的静态吸附量最小，表明该膜对蛋白的吸附能力相对最弱。91205

毕业论文关键词：PVDF超滤膜，分离性能，膜改性，凹土，静态吸附

Abstract: In this work, a pH-responsive inorganic-organic nanofiber, palygorskite-g-polyacrylic acid (PGS-g-PAA), was incorporated into PVDF matrix for hydrophilic modification。 The influence of dosages of the PGS-g-PAA on membrane structures and properties were investigated in detail。 The results show that as the increasing dosages of the modifier, the modified fouling index (MFI) decreased, and pure water flux (PWF) improved。 The PVDF/PGS-g-PAA hybrid membrane had the maximum retention rate for BSA when the PGS-g-PAA loading amount reaches 7。0 wt%。 When the PGS-g-PAA loading amount was 1。0 wt。%, the adsorption capacity for BSA was 237。5μg/cm2,which is smaller than that of pure PVDF membrane。

Keywords: PVDF ultrafiltration membrane, separation performance, membrane modification，palygorskite, static adsorption 

目  录

1  引言 3

1。1  超滤技术概述 3

1。2  超滤膜的选择 4

1。3  PVDF膜的改性 4

1。4  主要研究内容 6

2  实验部分 7

2。1  实验药品和仪器 7

2。2  混合基质超滤膜的制备 8

2。3  膜的纯水通量 8

2。4  膜的孔径测试 9

2。5  膜对BSA的静态吸来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766 附测试 9

2。6  膜分离性能测试 9

3  结果与分析 10

3。1  膜的纯水通量和孔径分析 10

3。2  膜对BSA的静态吸附分析 12

3。3  膜的分离性能分析 13

结  论 15

参 考 文 献 16

1  引言

1。1  超滤技术概述论文网

超滤技术属于膜分离技术，介于微滤与纳滤之间，它是利用膜表面微孔结构对各种物质进行选择性分离的新型流体分离技术。与传统的吸收、蒸馏与吸附相比较，它主要有以下几个特点：（1）常温进行，条件温和；（2）不发生相变，能耗小，不需加热；（3）分离系数相对较大，分离效率高；（4）装置简单，流程短，经济效益高；（5）无二次污染，节能环保。

1。1。1  超滤技术的原理

超滤又称为超过滤，超滤技术是一种膜过滤法。超滤膜的原理示意图如图1-1所示，当原液流经超滤膜，在超滤膜筛分时，以膜两侧的压力差为推动力，以膜为过滤介质，水中的大分子颗粒如细菌、蛋白质、胶体等被截留在原液内，它的截留范围从分子量为500的小分子到直径为0。2 μm的胶体粒子，而小分子溶质和水则可以通过膜壁上的微孔成为浓缩液，从而实现分离、分级、浓缩和净化的目的。