摘 要：利用超声化学法，以硝酸铈和草酸为原料，加入表面活性剂十六烷基三甲基溴化铵（CTAB），合成得到配位聚合物草酸铈微纳米多级结构。对获得的产物用X-射线粉末衍射（XRD)、红外(FT-IR)、热重(TGA)、紫外(UV)、荧光、比表面积检测法(BET)进行表征。通过扫描电镜(SEM)分析，研究了实验参数如反应时间和CTAB的用量对草酸铈形貌的影响。以草酸铈为前驱体，在空气氛中通过煅烧得到形貌遗传、尺寸可控的CeO2。93278

毕业论文关键词：微纳米结构、草酸铈、超声法、二氧化铈

Abstract:  Micro-nano meter hierarchical structure coordination polymer of cerium oxalate has been synthesized via an ultrasonic-assisted solution-phase method in the presence of surface active agent cetyltrimethylammonium bromide(CTAB)。 The as-prepared product was characterized by X-ray powder diffraction (XRD), FT-IR spectrum, thermogravimetric analysis (TG), ultraviolet(UV) spectra, fluorscence analysis and specific surface analysis。 By scanning electron microscopy (SEM), systematic investigations have been performed on the factors influencing the morphology of cerium oxalate micro-nano structures, such as reaction time and the amount of CTAB。 Finally, using the cerium oxalate as precursor and through calcination in atmosphere, CeO2 with controllable size has been obtained, which inherit uniform morphology from the precursor。

Keywords: micro-nano meter structure, cerium oxalate, ultrasonic method, CeO2

目  录

1。 前言 3

2。 实验部分 4

2。1 仪器 4

2。2 试剂 4

2。3 草酸铈的制备 4

2。4 二氧化铈的制备 4

3． 结果与讨论 5

3。1 草酸铈的XRD分析 5

3。2 草酸铈的FT-IR分析 6

3。3 草酸铈的TGA分析 7

3。4草酸铈的UV分析 8

3。5草酸铈的荧光分析 8

3。6 草酸铈的SEM分析 9

3。6。1 原料形态对草酸铈结构的影响 10

3。6。2 反应时间对草酸铈结构的影响 11

3。6。3 表面活性剂CTAB量对草酸铈结构的影响 15

3。6。4超声顺序对草酸铈结构的影响 19

3。7 煅烧类长方形草酸铈制得二氧化铈样品的分析 20

3。7。1 二氧化铈的XRD分析 20

3。7。2二氧化铈的N2吸脱附曲线及孔径大小 21

3。7。3二氧化铈的UV分析 21

3。7。4 二氧化铈的SEM分析 22

结   论 23

参考文献 24

致  谢 25

1。 前言

纳米材料是指晶粒尺寸为纳米级(10-9m) 的超细材料,它的微粒尺寸大于原子簇,小于通常的微粒,一般为 1~100nm[1]。纳米材料因其具有的独特的表面效应，体积效应以及量子尺寸效应，使材料的电学，力学，磁学，光学等性能产生了巨大的变化。纳米技术在精细陶瓷，微电子学，生物工程，化工，医学等领域的成功应用及其广阔的应用前景，使纳米材料及其技术成为目前科学研究的热点之一，纳米技术也被公认为是 21 世纪最具有前途的科研领域[2]。