摘 要：在没有表面活性剂的条件下，通过简单的水热法合成了纺锤状分级结构ZnGa2O4。XRD谱图表明所得ZnGa2O4晶化程度较好。FE-SEM和HR-TEM图像表明ZnGa2O4分级结构是由八面体ZnGa2O4组成的。并提出了这种纺锤状分级结构ZnGa2O4的可能形成机理。 室温光致发光显示，分级结构的ZnGa2O4在382，526和756 nm处具有三个发射带。通过在UV光照射下，通过降解亚甲基蓝（MB）来测试所得的ZnGa2O4的光催化性能。 结果表明，纺锤状分级结构ZnGa2O4具有良好的光催化活性。94028

毕业论文关键词：晶体生长，ZnGa2O4，性能

Abstract: In this paper， the formation of spindle shaped hierarchical ZnGa2O4 architectures was achieved through a facile hydrothermal method in the absence of any surfactants。 The XRD pattern indicated the formation of well crystallized ZnGa2O4。 The FE-SEM and HR-TEM images showed that the spindle shaped hierarchical ZnGa2O4 architectures were built by octahedral ZnGa2O4。 A possible formation mechanism for this kind of spindle shaped ZnGa2O4 structure was proposed。 Room temperature Photoluminescence shows that hierarchical ZnGa2O4 have three emission bands around at 382，526 and 756 nm。 The photocatalytic performance of the obtained ZnGa2O4 architectures was tested by the degradation of Methylene blue (MB) under UV light irradiation。 The result shows that spindle shaped ZnGa2O4 architectures have good photocatalytic performance。

Key Words: Crystal growth， ZnGa2O4，Properties

目  录

1 引言 4

1。1纳米材料的概述 4

1。1。1纳米材料的定义 4

1。1。2 纳米材料的特殊性质 4

1。1。3 纳米材料的应用 5

1。1。4 纳米材料的制备 7

1。2 纳米镓酸锌的应用和制备 7

1。3 本文主要研究内容 8

2 实验部分 8

2。1 仪器和试剂 8

2。1。1仪器 8

2。1。2 试剂 9

2。2 实验部分 9

2。2。1材料合成 9

2。2。2 材料表征 9

3 实验结果与讨论 9

3。1 X射线衍射表征结果 9

3。2 SEM和TEM表征结果 10

3。3 光催化性能研究 12

结 论 14

参 考 文 献 15

致 谢 18

1  引言

1。1  纳米材料的概述

1。1。1  纳米材料的定义来自优I尔Q论T文D网WWw.YoueRw.com 加QQ7520~18766

纳米材料是指具有纳米量级（1~100 nm）的晶态或非晶态超微粒构成的固体物质。世界上首次成功制备铁纳米粒子的化学家是德国科学家Gleiter等[1]，他们在1984年运用惰性气体凝聚法成功制备了铁纳米微粒，这标志着纳米材料进入了一个崭新的应用阶段。纳米材料在体积效应、表面效应、量子尺寸效应和宏观隧道效应等方面的性能明显不同于体材料，因此纳米材料在电子生产、化学化工、陶瓷制造、生物医药等诸多方面都有着重要应用，也引起人们的高度重视[2]。