摘要：优尔价铬钝化和三价铬钝化是目前应用最为广泛的镀锌层钝化工艺。但是优尔价铬是有毒物质，不仅会污染环境，并且对人的身体健康有非常大的危害。所以三价铬钝化工艺是电镀厂的首选工艺。三价铬钝化的膜层与优尔价铬钝化膜层有许多相似之处，但是其毒性仅是优尔价铬的1%。阐述了镀锌层在常温下得到三价铬彩色钝化膜的工艺。采用单因素实验法研究了钝化液的组份各自用量、操作条件对钝化膜外观的影响，采用中性盐雾试验测定了钝化膜层的耐腐蚀性。通过试验研究得到了三价铬彩色钝化工艺:三氯化铬为29.2g/L,硫酸钠为24g/L，氟化铵为1.2g/L，硝酸钠为12g/L,pH值2.5,钝化温度为30℃,钝化时间为60s。在该工艺中能获得的钝化膜表面光亮，呈彩虹色，允许有轻微雾；膜层与基底有良好的附着力，膜层的中性盐雾试验为72小时以上。32013
- 上一篇：南极假丝酵母脂肪酶的分子模拟
- 下一篇：罗丹明类新型荧光分子探针的合成及对铁离子的识别研究
毕业论文关键词：钝化；三价铬；镀锌
Study on temperature of trivalent chromium passivation technology of zinc layer surface
Abatract: Six valence chromium passivation and trivalent chromium passivation is one of the most extensive passivation process. But six chromium is a toxic substance, not only pollute the environment, and human health have very great harm. So the trivalent chromium passivation process is the preferred plating plant. The film of trivalent chromium passivation and six valence chromium passivation film have many similarities, but its toxicity is only six chromium 1%. This paper discusses the process of galvanized layer of trivalent chromium passivation film at room temperature. Using single facto. Using single factor experiment method and the optimization method, and study the influence of composition of the passivation solution of the respective dosage and operating conditions on the passivation effect. Through optimization experiment, trivalent chromium passivation process has been. By neutral salt spray test determination of the corrosion resistance of the film, through friction polishing experiments, determination of coating adhesion. Finally obtained plating surface was a rainbow color, the surface layer of the mask to look bright, light fog, the film and the substrate has good adhesion, film in neutral salt spray test for more than 72 hours, in accordance with the requirements of the project.
KeyWords: passivation; trivalent chromium; galvanized
目录
1 引言 1
1.1 课题的概况及研究意义 1
1.2 课题研究的内容及目的 2
1.3 课题在国内外研究的情况及发展趋势 3
1.4 课题主要的技术要求 4
2 三价铬钝化的技术原理 5
2.1 三价铬钝化机理 5
2.2 三价铬钝化膜和优尔价铬钝化膜外观比较 7
2.3 三价铬钝化膜外观的影响因素 7
2.3.1三价铬钝化剂组成及影响 7
2.3.2 钝化工作液pH值、钝化温度、浸渍时间影响 8
2.3.3 钝化膜干燥温度的影响 8
2.3.4杂质的影响 9
2.3.5 其他因素的影响 9
3 工艺研究方法 11
3.1工艺研究方法 11
3.2各项性能测定、试验方法 11
3.2.1钝化层性能试验方法 11
4 实验研究 13
4.1实验仪器和试剂 13
4.2镀锌层制备 13
4.2.1氯化钾镀锌溶液的配制 13
4.2.2电镀 13
4.3试片的钝化 13
4.3.1 钝化液的配制 13
4.3.2 试片的钝化 13
4.4 钝化层腐蚀性能检测 14
-
PS-b-PHEMA及其双组分嵌段共...
-
PS-b-PNIPAM单组份及其双组份...
-
ZnO/TiO2复合物的制备及光催化性能表征
-
MoS2/TiO2复合物的制备及光催化性能表征
-
ZnO/g-C3N4复合物的制备及光催化性能表征
-
ZnS纳米材料的制备与表征
-
CuS/g-C3N4复合物的制备及光催化性能表征
中国传统元素在游戏角色...
上市公司股权结构对经营绩效的影响研究
浅析中国古代宗法制度
巴金《激流三部曲》高觉新的悲剧命运
现代简约美式风格在室内家装中的运用
NFC协议物理层的软件实现+文献综述
高警觉工作人群的元情绪...
C++最短路径算法研究和程序设计
江苏省某高中学生体质现状的调查研究
g-C3N4光催化剂的制备和光催化性能研究