    摘要本文通过利用廉价生物质材料羧甲基纤维素钠优化仿生制备新型高效的CMC@PANI 复合材料并对优化得到的材料进行了 SEM、BET、XRD、UV-vis、FT-IR、TGA等表征。研究发现 pH=4，CMC 用量2.5g/L，Hemin 浓度为0.05g/L，0.07M H2O2，0.9M 盐酸掺杂，为 CMC@PANI 复合材料合成的最优条件。在此条件下合成的CMC@PANI同时对阴阳离子染料具有较高的吸附效率。此外，研究表明该材料对 pH 和温度有较宽的适应性，染料初始浓度和时间对 CMC@PANI 吸附 MO 的影响效果较为显著。RSM 优化CMC@PANI吸附MO的条件为：pH=7，C0=100mg/L，反应时间为 3h， 预测去除率值为99. 5%。该条件下，吸附符合准二级动力学和 Langmuir吸附等温方程，是自发、放热的物理吸附，在 323K时有最大吸附容量 294.12mg/g。与其他生物质吸附材料相比，CMC@PANI吸附容量大、条件温和，是较为理想的新型吸附剂。42427
    毕业论文关键词  CMC@PANI  仿生制备  吸附  染料 
     Title      The Preparation and Application of Cellulose-based   PANI Composite Adsorbent   
    Abstract Biomimetic Synthesis of cellulose-based composite absorbent CMC@PANI  were optimized in this paper and  the as-prepared  absorbent  were characteristic by  SEM, BET,  XRD,  UV-vis,  FT-IR and TGA. The data obtained from the  investigations indicated that the optimal conditions of CMC@PANI preparation is pH=4 adding 2.5g/LCMC, 0.05g/L Hemin and 0.07M H2O2 with 0.9M HCl doped at room temperature under which the  CMC@PANI  synthesized  demonstrated high adsorption  efficiency for both anionic and cationic dyes. CMC@PANI showed wide adaptability for MO removal in pH and temperature, while the removal rate was highly dependent on contract time  and the initial concentration  of dyes.  The RSM result suggested that  the best adsorption condition for CMC@PANI to remove MO was 3h under pH=7 with an initial concentration of 100mg/L, of which the removal ratio is predicted to be 99.5%. Furthermore, the adsorption under the selected condition implied that  the process was well described by pseudo-second order kinetic and Langmuir isotherm, which was an exothermic and spontaneous reaction controlled by physical adsorption. A comparison between CMC@PANI and other biomass adsorbents was carried out in this paper, providing that CMC@PANI was an ideal alternative with high adsorption capacity as well as respectively mild adsorption conditions.   
    Keywords    CMC@PANI  Biomimetic Synthesis  Adsorption   Dye

    目次

    1绪论..1

    1.1染料废水来源与危害.1

    1.2染料废水处理方法2

    1.3纤维素基吸附材料概述2

    1.3.1纤维素.2

    1.3.2纤维素基吸附材料..3

    1.4导电聚苯胺概述3

    1.4.1导电聚苯胺的合成..4

    1.4.2聚苯胺复合吸附材料.4

    1.5本文研究目的与内容.5

    1.5.1研究目的与意义5

    1.5.2研究内容6

    1.6技术路线图..6

    2CMC@PANI复合材料的制备方法优化及表征.8

    2.1实验部分.8

    2.1.1实验药品8

    2.1.2实验仪器8

    2.1.3材料制备与优化9

    2.1.4静态吸附吸附.9

    2.1.5样品表征9

    2.2实验结果与讨论.10

    2.2.1CMC@PANI制备中的影响因素..10

    2.2.2复合材料对不同染料的吸附效果13

    2.2.3样品表征.14

    3CMC@PANI复合材料吸附MO的影响因素及吸附条件的响应面优化17

    3.1实验部分..17

    3.1.1实验药品..17

    3.1.2实验仪器.17

    3.1.3单因素影响实验.17

    3.1.4响应面优化吸附条件18

    3.2实验结果与讨论.18

    3.2.1吸附条件影响..18

  1. 上一篇：聚多巴胺Ag复合纳米粒子改性聚醚砜（PES）超滤膜结构及性能研究
  2. 下一篇：接枝侧链型磺化聚芳醚质子交换膜的制备及其性能研究

  1. Cu2+诱导的硼-二吡咯亚甲基...

  2. 甲基咪唑衍生物荧光配体合成及其性能研究

  3. 羧基苯甲醛希夫碱合成及配合物性能研究

  4. 氨基噻吩荧光配体合成及性能研究

  5. Zn2GeO4光催化材料的形貌调...

  6. 基于柔性羧酸配体的MOFs的合成与晶体结构

  7. 铜基纳米材料的制备及性能研究

  8. 巴金《激流三部曲》高觉新的悲剧命运

  9. NFC协议物理层的软件实现+文献综述

  10. g-C3N4光催化剂的制备和光催化性能研究

  11. 中国传统元素在游戏角色...

  12. 江苏省某高中学生体质现状的调查研究

  13. 高警觉工作人群的元情绪...

  14. 上市公司股权结构对经营绩效的影响研究

  15. C++最短路径算法研究和程序设计

  16. 浅析中国古代宗法制度

  17. 现代简约美式风格在室内家装中的运用

　　

About

优尔论文网手机版...

主页：http://www.youerw.com

关闭返回