锑酸钡复合物的制备及应用

菜单

摘要：本论文实验通过改进常规锑酸盐的合成方法和路线，以三氯化锑和碳酸钠、碳酸钡为反应物，使用高温固相法，最终得到了产率高、纯净的锑酸钡，并以此改进的方法合成了系列锑酸稀土盐的复合物，通过对产物的紫外漫反射（DRS)、X射固体粉末线衍射（XRD)、扫描电镜（TEM）的检测结果分析，得到锑酸钡及锑酸稀土盐具有相同的结构。将锑酸钡和锑酸稀土盐粉末固体做三种同分异构硝基苯酚和甲基橙的催化降解实验，结果显示锑酸钡复合物及锑酸稀土盐均有很好的催化降解活性，降解率可达到90%以上，且性质稳定可多次用。51965

实验还研究了锑酸稀土盐中锑元素和稀土元素的不同摩尔质量比对于锑酸稀土盐有机降解活性的影响，得出的结果显示锑离子和稀土离子随着稀土元素的摩尔质量的增加使锑酸稀土盐的催化降解活性先增加后减小甚至消失。

毕业论文关键词：锑酸钡；稀土锑酸盐；锑酸盐；有机降解

Antimony acid barium compound preparation and application

Abstracts: This paper experiment by improving the synthesis method and route of conventional antimonate with antimony trichloride and sodium carbonate, barium carbonate for reactants, the use of high temperature solid phase method, finally obtained the high yield, and purity antimony acid barium, and the method of improving series antimony acid complexes of rare earth salt was synthesized, through to the product uv diffuse (DRS), X shoots the solid powder X-ray diffraction (XRD), scanning electron microscope (TEM) analysis of the test results, get acid barium antimony and antimony acid rare earth salt with the same structure. Will acid barium and antimony acid rare earth salt powder solid do with three points heterogeneous nitro phenol and methyl orange [1] [2] of catalytic degradation experiment, the results show that the acid barium compounds and antimony acid rare earth salt has good catalytic degradation activity, the degradation rate can reach more than 90%, and stable properties can be repeatedly used.Experiment also studied the antimony antimony elements and rare earth elements in rare earth salt acid of different molecular weight ratio for the influence of rare earth salt organic degradation activity of antimony acid, the results show that antimony ions and lanthanide ions with the increase of the molar mass of rare earth elements make antimony acid catalytic degradation activity of rare earth salt increased before they are reduced or even disappear.

Key words: Antimony acid barium；Rare earth antimonite；Antimonite; The organic degradation.

引言：锑酸钡复合物是一种重要的锑酸盐类化合物，可应用于半导体材料的合成与研究，还可以用于催化、光催化、荧光材料等方面，且锑酸钡的物理性良好，化学性稳定，由此使得锑酸钡复合物存在巨大的应用前景。二十一世纪以来，伴随工业的发展和科学技术的革新，精细化工的深入研究使得锑的重要性逐渐体现。锑的精细产品在半导体材料、军工、化工工业、航空航天、阻燃材料、LED 等方面应用广泛，拥有着极大的潜在经济和社会价值效益。

目前，锑酸盐的合成主要有水浴合成法、微波固相法、溶液--凝胶法、共沉淀高温固相法、蒸发溶剂热解法等传统方法。虽然共沉淀高温固相法因为生成沉淀在溶液中的溶解度不同而难以控制终产物的摩尔系数比，可是共沉淀法在溶液中的溶解度小，操作简单，方便快捷而在实验中经常用到。如Hongli Liu 通过共沉淀高温固相法法成功的向AnSbmOz：B3+(n1m、z=1、2、3.....，B代表稀土元素)体系引入卤素离子，使产品的发光性能大大提高;杨绪勇等人则成功的对锑酸钡体系引入卤素离子进行电荷补偿，使其吸光范围扩宽，增强了产物的荧光性。水浴合成法能合成均相分撒的纳米级颗粒的产物，但是反应时间较长，产率低，其他方法同此两种方法缺点大致相同。