摘要：本文中，在水溶性高分子羧甲基纤维素钠晶体生长调节剂存在的条件下，通过水热法大面积合成了新颖中空花生状CuO。通过X射线衍射(XRD)，场发射扫描电子显微镜(FE-SEM)和透射电子显微镜(TEM)表征研究所得到的样品，提出了中空花生状CuO可能的形成机理。此外，对所得CuO样品的催化性能进行了研究，发现这些具有中空花生状结构的CuO有很好的加快高氯酸铵(复合固体推进剂的重要的氧化剂)热分解的能力。52061
毕业论文关键词：氧化铜，花生状，中空
Abstract: In this study, novel peanut shaped CuO hollow architectures have been synthesized on a large scale through a facile one-pot hydrothermal method in the presence of water-soluble biopolymer sodium carboxymethyl cellulose as crystal growth modifiers. The as-obtained samples were investigated by a set of characterizations including field emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD) pattern. A possible formation mechanism of this kind of peanut shaped CuO hollow architectures has also been proposed. Furthermore, the catalytic properties of as-obtained samples were investigated. It was found that these as-obtained peanut shaped CuO hollow architectures have good abilities to accelerate the thermal decomposition of ammonium perchlorate, an important oxidizer in composite solid propellants.
Key words: Cupric oxide, peanut shaped, hollow
目 录
1 引言 4
1.1纳米材料的概述 4
1.1.1纳米材料的定义 4
1.1.2 纳米材料的奇异特性 4
1.1.3 纳米材料的应用 4
1.1.4 纳米材料的制备 6
1.2 纳米氧化铜的应用和制备 6
1.3 本文主要研究内容 7
2 实验部分 7
2.1 仪器和试剂 7
2.1.1仪器 7
2.1.2 试剂 8
2.2 实验部分 8
2.2.1材料合成 8
2.2.2 材料表征 8
3 实验结果与讨论 8
3.1 X射线衍射表征结果 8
3.2 SEM和TEM表征结果 9
3.3 生长机理探索 10
3.4 催化分解性能研究 10
结 论 12
参考文献 13
1 引言
1.1 纳米材料的概述
1.1.1 纳米材料的定义
纳米材料又称超微细材料，是由超微颗粒——绝大多数是晶体，其特征尺寸在纳米量级（通常指1 – 100 nm）——组成的固体材料[1]。图1为各种纳米结构的照片。从广义上讲，纳米材料是指三维空间尺寸中至少有一维处于纳米量级的材料[2]。从狭义上讲，则主要包括纳米微粒及由它构成的纳米固体（体材料与微粒膜）[3]。纳米是长度单位量度，1 nm = 10-9 m，大约为4到5个原子排列起来的长度。
各种纳米结构的照片：（a）纳米颗粒，（b）纳米线，（c）纳米带
1.1.2 纳米材料的奇异特性
随着物质超微化，纳米材料表面电子结构和晶体结构也随之发生变化，进而使其具有一系列特异效应。