摘要：石墨烯是一种由碳原子构成的单层片状结构的新材料，由于石墨烯材料的特殊性能使得石墨烯在各个领域得到广泛的应用。而石墨烯复合材料由于具有更优异的性能，使得其具有更加广阔的发展前景。本文以氧化石墨为原料，通过化学还原制备石墨烯-壳聚糖复合材料，进行了扫描电子显微镜和比表面分析，确定复合材料的微观形貌和结构。比表面分析显示，冷冻干燥后复合材料的比表面为80.4m2/g。探讨石墨烯-壳聚糖复合材料对水体中重金属离子的吸附作用，研究复合材料对重金属离子的最佳环境。56013
毕业论文关键词：石墨烯，复合材料，铜离子，吸附
Abstract: Graphene is a kind of new material with carbon atom monolayer sheet-like structure, due to the unique properties and structure graphene have been widely used in various fields such as catalysis, biosensors and energy storage. Because their very attractive performance graphene-based composites will show much bright furture in these application areas. In this paper, using graphite oxide as raw material, graphene-chitosan composite was prepared by chemical reduction. The microstructure and morphology was characterized by scan electron microscope and specific surface ared analyzer. The reaults show that graphene-chitosan compsite has much pores with the BET surface area 80.4 m2/g after lyophilization. Using this composite as absorbent the absorption performance was investigated in detail to obtain the optimal conditions for the removal of heavy-metal ion in water.
Keywords: Graphene, composite materials, copper ion, adsorption
目 录
１ 前言 3
1.1石墨烯的简介 3
1.1石墨烯的发现史 3
1.2石墨烯的制备方法 4
1.3 石墨烯的应用 4
1.4 石墨烯复合材料对水中重金属的吸附 5
2 实验部分 6
2.1仪器和试剂 6
2.2实验步骤 6
2.2.1氧化石墨的制备 6
2.2.2石墨烯-壳聚糖复合材料的制备 7
2.2.3铜离子标准工作曲线的绘制 7
2.2.3石墨烯-壳聚糖复合材料对水中铜离子的吸附 7
3 结果与讨论 7
3.1 石墨烯-壳聚糖复合材料的合成与表征 7
3.2 石墨烯-壳聚糖复合材料对铜离子的吸附性能 9
3.2.1铜离子标准工作曲线 9
3.2.2时间对复合材料吸附性能的影响 9
3.2.3 PH值对复合材料吸附性能的影响 10
3.2.4吸附剂用量对复合材料吸附性能的影响 11
结论 12
参考文献 13
致谢 14
1 前言
1.1 石墨烯的简介
石墨烯（Graphene）一直被认为是假设性的结构，无法单独稳定存在。直到2004年，英国曼彻斯特大学的安德烈·海姆和康斯坦丁·诺沃肖洛夫成功地在实验中从石墨中分离出石墨烯，从而证实石墨烯可以稳定存在，二人也因“在二维石墨烯材料的开创性实验”共同获得2010年诺贝尔物理学奖。