摘要:通过一个简单的氧化还原路线,对ZnO进行不同程度的表面处理。随后对经过表面处理的氧化锌材料的形貌、表面结构、粒径大小等特性进行了表征。,分别是X射线衍射,N 2物理吸附测量,紫外可见,PL光谱,SEM,TEM和二氧化碳吸附的FTIR。表征结果证实,表面处理后所得的ZnO复合材料具有高比表面积,能减小光的吸附能力,并且不会影响晶体结构的优点。通过反应性能和CO2-FTIR发现,适当的表面氧化处理可以有效地促进CO2吸附和增强生成的b-CO32-中间体,调高H2O2浓度后ZnO催化剂的甲烷产量是纯的ZnO催化剂的上百倍。同时,延长反应时间,ZnO催化剂更偏向于CO2和H2O混合选择性生成CH3OH。可能是由于电子迅速分离传送到催化材料表面的OH基团,这直接关系到甲醇的产量。61831

毕业论文关键词:氧化锌;二氧化碳光催化;二氧化碳吸附中间体;表面处理

Effect of ZnO surface treatment on photocatalytic reduction of CO2

Abstract: Through a simple redox route, the ZnO were treated with different degrees of surface treatment. The morphology, surface structure, particle size and other characteristics of the surface treated Zinc Oxide were characterized. X ray diffraction, N 2 physical adsorption measurements, UV Vis, PL spectroscopy, SEM, TEM and carbon dioxide adsorption of FTIR. Characterization results show that the surface treatment of the resulting ZnO Composite with high specific surface area, can reduce the adsorption capacity of Hikari and will not affect the crystal structure of the advantages. Appropriate surface oxidation treatment can effectively promote adsorption of CO2 and enhanced generation of b-CO32- intermediates, adjustable high H2O2 concentration ZnO catalyst for methane production is a hundred times more than that of the pure ZnO catalyst, found through the reaction performance and CO2-FTIR. At the same time, increasing the reaction temperature, ZnO catalyst is more inclined to the CO2 and H2O mixed selective generation CH3OH. May be due to the rapid separation of electrons transferred to the catalytic material surface of the OH group, which is directly related to the production of methanol.

Keywords: Zinc Oxide; carbon dioxide photo catalysis; carbon dioxide adsorption intermediate;

摘要 i

Abstract i

1. 文献综述 2

1.1 研究的意义 2

1.2 研究进展 3

1.3 ZNO的晶体结构 4

1.4 提高光催化的途径 5

1.4.1 半导体复合 5

1.4.2 离子掺杂 5

1.4.3 表面贵金属沉积 5

1.4.4 表面敏化 6

2. 实验部分 6

2.1 药品试剂及实验设备 6

2.1.1 试剂 6

2.1.2 实验器材 6

2.2 半导体材料的制备

上一篇:年产1000吨洗模胶车间工艺设计
下一篇:MFe2O4-ZnO半导体材料的制备以及阳离子对其光催化还原CO2性能的影响

水热法制备ZnO和性能研究

ZnO/碳纳米复合纤维的制备...

ZnO/TiO2复合物的制备及光催化性能表征

ZnO/g-C3N4复合物的制备及光催化性能表征

纳米ZnO的掺杂改性及光催化性能究

无极性ZnO薄膜的制备和表征研究

ZnO/TiO2复合材料的制备及其光催化性能研究

安康汉江网讯

LiMn1-xFexPO4正极材料合成及充放电性能研究

互联网教育”变革路径研究进展【7972字】

网络语言“XX体”研究

张洁小说《无字》中的女性意识

老年2型糖尿病患者运动疗...

麦秸秆还田和沼液灌溉对...

ASP.net+sqlserver企业设备管理系统设计与开发

新課改下小學语文洧效阅...

我国风险投资的发展现状问题及对策分析