摘要热熔胶具有软化点高，耐热性好，耐低温性好，耐化学性优良等环境友好型特点，成为市场的主流，越来越多的人加入对热熔胶性能的改良的研究。本论文主要研究二聚酸与不同胺单体缩合制成二聚酸聚酰胺热熔胶，以提高热熔胶的软化点，增强醇溶性等为目的，通过加入不同配比的胺单体，测试产物的性能，即熔点、酸胺值、溶解性、熔指、黏度以及表征，来确定最佳配比和最佳性能的胺单体，获得最佳性能的二聚酸聚酰胺热熔胶，以便公司进行大规模批量生产。62404

Hot melt adhesive having a high softening point, good heat resistance, good low temperature resistance, excellent chemical resistance and other environmentally friendly features into the mainstream of the market, more and more people join effect on improving the performance of hot melt adhesive. In this thesis, dimer acid and amine monomers different condensation formed dimer acid polyamide hot melt adhesive, hot melt adhesive to increase the softening point, for the purpose of enhancement of alcohol, by adding different ratios of amine monomer, performance testing products, namely melting point, acid amine value, solubility, melt index, viscosity and characterization, to determine the optimal ratio of amine monomer and the best performance, the best performance of the dimer acid polyamide hot melt adhesive for large-scale production companies.

毕业论文关键词：二聚酸聚酰胺热熔胶； 己二胺； 最佳配比；软化点； 熔指； 表征

Keyword: Dimer acid polyamide hot melt adhesive； Hexamethylene diamine； The best ratio；Softening Point； Flow rate； Characterization

目    录

第一章 绪论 4

1.1前言 4

1.2二聚酸聚酰胺热熔胶的研究现状 5

1.2.1对IPDA的认识 5

1.2.2对哌嗪的认识 5

1.2.3对三甲基己二胺的认识 6

1.2.4对Dytek A的认识 6

1.3二聚酸聚酰胺热熔胶的工艺及技术 7

1.3.1工艺原理 7

1.3.2缩聚反应加胺工艺 7

1.3.3基本工艺流程 8

1.4本文的研究目的及其意义 8

第二章 二聚酸聚酰胺的合成 9

2.1实验仪器与原料 9

2.1.1实验仪器 9

2.1.2 实验原料 10

2.2实验和测试部分 10

2.2.1二聚酸聚酰胺热熔胶的合成 10

2.2.2二聚酸聚酰胺热熔胶的性能测试 12

2.3实验结果与讨论 15

2.3.1二聚酸聚酰胺热熔胶的熔点变化 15

2.3.2二聚酸聚酰胺热熔胶的酸值胺值变化 16

2.3.3二聚酸聚酰胺热熔胶的粘度变化 16

2.3.4二聚酸聚酰胺热熔胶的溶解度 17

2.3.5二聚酸聚酰胺热熔胶的熔指的变化 18

2.3.6二聚酸聚酰胺热熔胶的表征 18

第三章 结论 19

第一章 绪论

1.1前言