摘要：利用对硝基苯异硫氰酸酯对凹凸棒土进行改性并利用红外、X射线衍射、比表面等对改性前后凹凸棒土进行表征。结果表明，对硝基苯异硫氰酸酯有效地以化学键的形式结合到凹凸棒土表面，但没有改变凹凸棒土层状构造。测定了改性后的凹凸棒土对亚甲蓝的吸附能力。常温下，在亚甲基蓝浓度为15mg/L溶液中加入改性凹土加入量为5g/L、脱色时间50min，对亚甲基蓝吸附率为99%以上。64402

毕业论文关键词：对硝基苯异硫氰酸酯，凹凸棒土,有机改性, 亚甲基蓝

Abstract：The attapulgite powders were organically modified using 4-nitrophenyl isothiocyanate. The pristine and modified attapulgite powders were characterized by IR, XRD, BET. The results showed that the main interaction between attapulgite surface and 4-nitrophenyl isothicyanate are chemical bonds. The structures of attapulgite has unchanged. The quantity of modified attapulgite powders, adsorption time and temperature on the adsorption effect of methylene blue were investigated. When modified attapulgite powders adds to about 5g /L, methylene blue density 15mg /L, room temperature, around 50min, the decolorization rate of methylene blue reached 99.2%. 

keyword: 4-nitro isothiocyanate, attapulgite powder, organically modify, methylene blue

1 引言 4

2 实验部分 4

2.1试剂和仪器 4

2.1.1 试剂 4

2.1.2 仪器 4

2.2 改性凹凸棒土的制备 4

2.2.1凹凸棒土的盐酸处理 4

2.2.2氨基凹土的制备 5

2.2.3改性凹凸棒土的制备 5

2.3 改性凹土对亚甲基蓝的吸附实验 5

3.结果与讨论 5

3.1改性凹凸棒土的表征 5

3.1.1红外光谱分析 5

3.1.2 X-射线(XRD)分析 7

3.1.3比表面分析 9

3.2 改性凹凸棒土对亚甲蓝吸附测试 10

3.2.1 亚甲基蓝最大吸收波长的确定 10

3.2.2 凹凸棒土的加入量对吸附平衡的影响 10

3.2.3时间对吸附平衡的影响 11

3.2.4 温度对吸附平衡的影响 12

3.2.5吸附等温线.....12

结 论 14

参考文献 15

致  谢 16

1 引言 

凹凸棒土是一种具有独特的层链状结构特征的晶质水合镁铝硅酸盐矿物，在江苏省眙盱县境内分布广泛，占全国凹土储藏量的73%，有着“千土之土”的美誉。然而我国凹土利用率低，附加产品开发应用少，价格低廉[1-3]。作为制造业大国，我国染料行业发展迅速[4-6]，每年约有130亿吨的染料废水排入各类水体，对水资源造成了污染，对环境造成了破坏[7-9]。因此选择一种吸附试剂用以去除染料废水中的染料具有非常重要的前景。本文考虑以4－硝基苯异硫氰酸酯对对凹凸棒土进行有机改性，测试改性后的凹凸棒土对有机染料亚甲基蓝为吸附质的吸附能力，为以后利用凹凸棒土处理印染污水提供依据。

2 实验部分

2.1试剂和仪器