摘要：TiO2纳米复合材料具有比表面积大，化学稳定性好，光催化性能优异等性质，在氙灯照射下能够将有机染料降解为二氧化碳和水。本文主要进行了二氧化钛-氧化石墨烯（TiO2-GO）、活性炭负载二氧化钛-氧化石墨烯（TiO2-GO-AC）的制备实验，讨论了氙灯条件下纳米二氧化钛复合材料催化降解有机染料罗丹明B的降解效率，同时，介绍了二氧化碳纳米复合材料降解有机染料的机理和应用前景。69866

毕业论文关键词：二氧化钛、光催化、活性炭、氧化石墨烯、有机染料降解

The preparation and application of TiO2 nanocomposites in degrading organic dyes

Abstract: TiO2 nanocomposites have potential to degrade some organic dyes into CO2 and H2O with xenon lamp due to its excellent properties, such as high surface area，good chemical stabilty and excellent photocatalytic capability. The preparation of titanium dioxide - graphene oxide (TiO2 - GO) and activated carbon load titanium dioxide - graphene oxide (TiO2 - GO - AC) as well as its degradation efficiency of rhodamine B with xenon lamp are mainly experimented in this thesis. And the mechanism and application prospect of titanium dioxide nanocomposite material in degradation organic dyes are also mentioned.

Keywords: Titanium dioxide; photocatalytic; activated carbon; graphene oxide; 

organic dyes degradation

目录

摘要 1

Abstract 1

1前言 2

1.1选题依据和意义 2

1.2 TiO2材料的研究现状 2

1.3石墨烯 3

1.3.1石墨烯的化学改性 4

1.3.2石墨烯复合材料 5

1.4活性炭 5

1.5有机染料 6

2 TiO2光催化降解罗丹明B的性能研究 7

2.1 实验部分 7

2.1.1实验仪器和试剂 7

2.2.2 TiO2光催化罗丹明B 8

2.2结果与讨论 8

2.2.1 TiO2光催化下不同时间的罗丹明B的吸光度 8

2.2.2 TiO2光催化降解效率 9

2.3小结 9

3 二氧化钛-氧化石墨烯纳米复合材料的制备及光催化性能的研究 10

3.1实验部分 10

3.1.1实验仪器与试剂 10

3.1.2二氧化钛-氧化石墨烯纳米复合材料的制备 10

3.1.3 TiO2-20%GO光催化罗丹明B 10

3.2结果与分析 10

3.2.1 TiO2-20%GO光催化下不同时间的罗丹明B的吸光度 10

3.2.2 TiO2-20%GO 光催化降解效率 11

3.3小结 11

4 活性炭负载二氧化钛-氧化石墨烯复合材料的制备及光催化性能的研究 12

4.1实验部分 12

4.1.1 实验仪器与试剂 12

4.1.2活性炭的预处理 12

4.1.3 活性炭负载二氧化钛-氧化石墨烯复合材料的制备