摘要本论文首先对目前新型含能材料降感的方法进行简单的介绍，利用相分离法对 HMX 进行表面包覆，并对 HMX 包覆过程中包覆剂的使用和包覆剂含量的使用以及对影响包覆 效果的因素进行分析，使得包覆能够更加理想。所选用的包覆材料包括 F2604-2 和 DOS， 通过 XPS 和扫描电镜观察包覆后的表征，最后测试包覆产品的机械感度，发现 F2604-2 和 DOS 都可以有效的包覆在 HMX 表面，并且都有着不同程度的降感作用，且 DOS 降感 的效果好于 F2604-2。78040

毕业论文关键词 降感 相分离法 机械感度 包覆

毕 业 设 计 说 明 书 外 文 摘 要

Title The research on new energetic materials

Abstract In this paper, the methods to reduce sensitivity of new energetic materials are simply introduced, and phase separation process are used to test the  HMX。 To make the coating more ideal, the influence of the coating agent on coating effects were studied。F2604-2 and DOS were coated on HMX。The results were charactered by XPS and SEM。 The mechanical sensitivity measurement found that both DOS and F2604-2 can be coated efficiently, with the effects to reduce sensitivity。 But the coating effect of DOS is better than F2604-2。

Keywords reduced sensitivity phase separation  process  mechanical sensitivity   coating

本科毕业设计说明书 第 I 页

目 录

1 绪论 1

1。1 研究背景和意义 1

1。2 含能材料降感的方法和途径 1

1。3 炸药包覆的研究进展 2

1。4 含能材料的包覆方法 3

1。5 研究任务和思路 5

2 实验仪器与实验药品 7

2。1 实验仪器 7

2。2 实验试剂 7

3 橡胶类包覆含能材料样品的制备及其性能的研究 8

3。1 顺丁橡胶包覆 HMX 样品的制备及其性能的研究 8

3。2 F 橡胶包覆 HMX 样品的制备及其性能的研究 9

3。3 微石蜡包覆 HMX 样品的制备及其性能的研究 10

4 F2604-02 和 DOS 包覆样品的制备及机械感度的测试 12

4。1 实验药品 12

4。2 实验步骤 12

4。3 包覆样品的表征 12

4。4 小结 16

结 论