摘要TC4钛合金强度高，耐腐蚀性好，但是硬度较低，耐磨性较差。因此，本实验通过等离子阴极沉积技术（PED），在钛合金的表面制备含ZrO2的多孔陶瓷膜层，以此来提高其硬度和耐磨性能。实验中，通过改变交流电压的大小和反应时间的长短来获得不同工艺下的试样。利用XRD、SEM、磨损仪、台阶仪等对每个试样进行物相、形貌、摩擦性能的分析。最终得到以下结论，350V电压下处理试样30min为最佳的实验方案。此工艺下，涂层表面形貌均匀、细密，硬度和耐摩擦性能最佳，因此该方法能有效提升钛合金的硬度和耐磨性能。87802

毕业论文关键词 等离子阴极沉积 ZrO2陶瓷 表面改性

毕 业 设 计 说 明 书 中 文 摘 要

Title Research on the preparation of compound coating ZrO2    on the surface of TC4 via plasma electrolytic         

Abstract Surface engineering techniques are widely used to improve the surface wear resistance and hardness of TC4。 In this dissertation, ZrO2 composite coating that aimed at improving the wear resistance and corrosion resistance of TC4 substrate of TC4 were produced by cathodic plasma electrolytic deposition process (CPED)。 The surface structure and their corresponding elemental composition of the coating were obtained by SEM, which was equipped with EDS。 Coating phases were analyzed via XRD。 The friction property and corrosion behavior were detected by specific machines。By this way we can prepare the best specimen with high surface wear resistance and hardness。

Keywords  Plasma cathode electrodeposition     ZrO2 ceramic   Surface modification

目    次

1  绪论 1

1。1  引言 1

1。2  现阶段常用的钛合金表面改性方法 2

1。3  液相阴极等离子电解沉积技术的研究现状 3

1。4  液相阴极等离子电解沉积技术 5From+优`尔^文W网wWw.YouErw.com 加QQ75201^8766

1。5  课题相关TC4表面改性研究现状 7

1。6  本课题的内容 8

2  实验研究方法 9

2。1  实验材料及设备 9

2。2  涂层制备参数 10

3  分析与结论 11

3。1  形貌分析 11

3。2  EDS能谱分析 13

3。3  物相分析 13

3。4  截面形貌分析 15

3。5  截面硬度分析 16

3。5  磨损性能 17

结  论 19

致  谢 20

参 考 文 献 21

1  绪论

1。1  引言

从上个世纪50年代开始，钛就作为一种重要的结构金属被人们发掘、使用，而钛合金工业的发展程度也成为了衡量一个国家综合国力和工业水平的重要指标[1-2]。现如今，钛合金因其具有多种优良性能例如比强度高、无磁性、无毒性，同时具有优良的耐腐蚀性能，且易与生物组织进行稳固的结合、使用温度范围广[3]，早已成为全球新兴的功能材料、耐腐蚀结构材料和生物工程材料，广泛应用于航天[4]、兵器、化工、冶金、船舶、海洋开发和卫生、记忆合金等领域。源-于,优Y尔E论W文.网wwW.yOueRw.com 原文+QQ752018`766