摘要本论文主要以宝磁的酸再生氧化铁为主要原材料，通过表面改性，改变其颜色性质。XRD、SEM、XRF、SIZE等方法进行表征结构、形貌的变化。结果表明：宝磁氧化铁红属于α-Fe2O3，适用于颜料铁红；聚丙烯酸树脂包覆时，当BET7聚丙烯酸树脂包覆量为6%时，BET7和BET14（6:4）包覆量为2%时，BET7和BET14（5:5）包覆量为2%，所获得的样品结构不变，形貌圆滑；分别与市售彩乐190、彩乐130和市售洛克产品颜色一致。35029
- 上一篇：有机磷阻燃剂对聚氨酯硬泡阻燃性能的影响
- 下一篇：反蛋白石结构ZnO、TiO2光催化薄膜的制备及其性能研究
毕业论文关键词：氧化铁红；改性；着色度
Abstract In this paper, the iron oxide from acid regeneration in BaoSteel was used as starting material. The surface modification methods were applied to improve its colour performance. Typically, XRD, SEM, XRF and SIZE were employed to test the change of micro-structure and morphology of iron oxide. The results indicated the iron oxide from BaoSteel was ascribed toα-Fe2O3, and could be utilized to be the iron red pigment. When the polypropylene resin(PPR) was coated, the iron oxide with different specific surface area of 7 and 14m2/g could keep theα-Fe2O3. Moreover, the sample of BET7 with 6%, the sample of BET14:BET7（5:5）with 2%, the sample of BET14:BET7（6:4）with 2% PPR are similar to the commercial caile190, caile130 and Luoke.
Key words: iron oxide red ; modified; pigmentation degree;
目 录
摘 要 1
1绪论 1
1.1 氧化铁红颜料概述 1
1.1.1 氧化铁红的晶型结构 1
1.1.2颜料氧化铁红的性质 2
1.1.3颜料氧化铁红的用途和研究现状 5
1.2 酸再生氧化铁红 7
1.2.1酸再生氧化铁红的工艺流程 7
1.2.2纯度和杂质含量对酸再生氧化铁粉的影响 10
1.2.3 BET对酸再生氧化铁粉的影响 10
1.3本论文主要研究内容 10
2实验部分 12
2.1 实验原料及实验仪器设备 12
2.2实验过程 13
2.2.1刮样操作步骤 13
2.2.2聚丙烯树脂改性 17
2.2.3 BET=14和BET=7不同比例混合 18
2.2.4硝酸改性 18
2.3表征手段 18
3结果与讨论 19
3.1酸再生氧化铁红和颜料铁红的对比性研究 19
3.1.1 XRD物相分析 19
3.1.2激光粒度仪分析 22
3.1.3 磁性能分析 25
3.1.4 SEM形貌分析 26
3.1.5 TEM分析 32
3.2水洗铁红的的改性研究 33
3.2.1BET=14和BET=7复配研究 33
3.2.2表面包覆改性 37
3.2.3 HCl消除反应 42
3.2.4本章小结 45
4结论 47
致谢 48
参考文献 48
1 绪论
1.1 氧化铁红颜料概述
氧化铁红（Iron Oxide Red），化学式为Fe2O3，平常也被称为铁红、锈红和铁氧红等。氧化铁红有考证的是从两万年前开始使用，现在是工业上继钛白粉后的一种重要的无机颜料，呈红色或深红色无定型的粉末状。
1.1.1 氧化铁红的晶型结构
Fe2O3有两种晶型，一种是立方体结构，另一种是菱型结构，其中α-Fe2O3属菱型结构，γ-Fe2O3则属于立方结构，两者之间的物相均属于hematite（赤铁矿），rhombohedral（菱方晶系）[1]（图1.1）。