摘要：本文主要研究了高铁的接触线在生产过程中出现的缩孔问题。发现熔液温度，粘度纯净度，冷却强度和上引速度均对缩孔形成有影响。实验结果表明：在上引连铸生产中，冷却强度越高，越不容易产生缩孔，冷却强度越低，越容易产生缩孔，冷却强度以25-30l/min为宜。初始温度越高，越容易产生缩孔。上引速度越快，越容易产生缩孔，上引速度最好225mm/min-261 mm/min之间不容易产生缩孔。冷却水进水温度高，冷却强度越低，缩孔形成概率越大。36835
- 上一篇：吸附树脂去除混合溶液中的有毒物质的研究
- 下一篇：多铁性复合材料的制备与性能研究
毕业论文关键词：上引连铸；缩孔；冷却强度
Mechanism on center of shrinkage cavity of Magnesium copper alloy rod with continuous up-casting
Abstract: This paper mainly studied the high iron contact line shrinkage cavity of the problems in the process of production. Found molten temperature, cooling intensity and the lead-rate all have an impact on shrinkage cavity formation. The experimental results show that in the continuous casting production, the higher the cooling intensity, the less prone to shrinkage, the higher the initial temperature, the more prone to shrinkage cavity. The lead faster, more prone to shrinkage, the best speed is not prone to shrinkage lead between 228mm/min-261mm/min.cooling water inlet temperature is high ,the lower the cooling intensity, the greater the probability of shrinkage cavity formation.
Keywords: The continuous up-casting；shrinkage cavity；cooling intensity
目录
1.前言 1
1.1高速铁路用接触线的种类及特点 1
1.1.1.高铁用接触线的加工方法 1
1.1.2.高铁对接触线要求 2
1.2铜镁合金接触线的生产 2
1.3上引连铸简介 3
1.4.上引连铸缺陷 4
1.5上引连铸铜镁合金杆中心缩孔形成影响因素 5
1.5.1.溶液粘度 5
1.5.2.熔液温度 5
1.5.3.熔液纯净度 5
1.5.4.冷却速度 6
1.5.5.上引速度 6
1.6选题的目的和意义 7
1.7课题的研究内容和目标 7
1.7.1.研究内容 7
1.7.2.研究目标 7
2.实验 9
2.1试验材料 9
2.2试验方法 9
2.2.1.缩孔诊断 9
2.2.2.上引连铸工艺参数对铜镁合金杆中心缩孔形成的影响 9
2.3实验设备 10
2.3.1.上引连铸机 10
2.3.2.金相显微镜 11
2.3.3.扫描电镜 11
2.3.4.抛光机 12
2.4试验过程 12
-
630不锈钢连铸结晶器保护渣物理性能研究
-
碳包硫化亚铁纳米颗粒的合成及在锂电上应用
-
纳米ZnO/上转换复合材料制...
-
渗碳体纳米复合颗粒合成及在锂电上的应用
-
上引连铸铜合金的组织和性能研究
-
钢上双丝堆焊Fe-Al层的组织性能研究
-
钢上双丝堆焊Fe-Al层的工艺试验研究
巴金《激流三部曲》高觉新的悲剧命运
g-C3N4光催化剂的制备和光催化性能研究
上市公司股权结构对经营绩效的影响研究
现代简约美式风格在室内家装中的运用
中国传统元素在游戏角色...
浅析中国古代宗法制度
C++最短路径算法研究和程序设计
江苏省某高中学生体质现状的调查研究
高警觉工作人群的元情绪...
NFC协议物理层的软件实现+文献综述