La3Co2SbO9的合成及磁性研究

菜单

摘要钙钛矿和双钙钛矿结构材料在压电、超导、磁电阻、催化、离子导体等领域有广泛的应用，是当前材料科学研究领域的热点之一。La3Co2SbO9是由G. Blasse首先发现的， D.G.Franco对La3Co2SbO9的结构和磁特性进行了初步研究，但其样品存在一定的缺陷，对其磁性质还不是很清楚。我们通过固相反应法得到纯净的样品，并对其磁性质进行了详细的研究。48458

Because of the possible application in piezoelectric materials, superconductivity, magnetoresistance, catalysis, ionic conductor etc. Double perovskite and perovskite materials had attracted much attention in the scientific field. La3Co2SbO9 firstly found by G. Blasse .The structure and magnetic properties were studied by D. G. Franco. Because of some impurities to the sample, the magnetic properties are still unclear up to now. We synthesis the La3Co2SbO9 by use of the solid state method, and get the pure samples, and study the magnetic properties of this sample.

毕业论文关键词：La3Co2SbO9；双钙钛矿；粉末X射线衍射；磁性测量系统；核磁共振系统

Keyword: La3Co2SbO9； Double perovskite； Powder X-ray Diffraction；MPMS (SQUID) VSM；NMR

第一章简介4

第二章实验方法·5

2.1.固相合成法5

2.2.样品制备··6

第三章样品评价·7

3.1. X-ray Powder Diffraction（XRD）··7

3.1.1. XRD使用原理·7

3.1.2. 样品La3Co2SbO9的XRD测量步骤··8

3.2. MPMS 磁性测量系统8

3.2.1. MPMS(SQUID) VSM系统简介8

3.2.2. La3Co2SbO9磁化率测量步骤····9

3.2.2.1.弱场下的磁化率测量步骤····9

3.2.2.2.强场下的磁化率测量步骤····9

3.3.核磁共振测量系统9

3.3.1.核磁共振仪使用原理和系统简介···9

3.3.2.核磁共振测量步骤10

第四章实验结果··10

4.1.结构特征···10

　　4.1.1.XRD测量结果·10

　　4.1.2.La3Co2SbO9晶格结构11

4.2.磁化率测量结果··12

4.2.1.弱磁场下的磁化率测量结果··12

4.2.2.磁化率与温度的变化关系测量结果·13

4.2.3.强磁场下的磁化率测量结果·13

4.3.核磁共振测量结果14

第五章结论·14

第六章参考文献··15

第七章感谢·16

第一章、简介

在现今研究领域钙钛矿和双钙钛矿结构的材料的研究是备受瞩目的。在压电、超导、磁电阻、催化、离子导体等多种功能材料中，具有钙钛矿结构的材料占有重要比例，因此钙钛矿结构材料是当前材料科学研究领域的热点之一。

钙钛矿是指一类陶瓷氧化物，此类氧化物最早被发现,源^自#优尔^文~论`文{网[www.youerw.com，是存在于钙钛矿石中的钛酸钙(CaTiO3)化合物，因此而得名。简单钙钛矿的一般组成是ABO3，因其分子式中各元素比例为1:1:3，所以又称“113结构”，钙钛矿是一种复合金属氧化物，呈立方体晶型，在高温变体结构中，钛离子位于立方晶胞的中心，为12个氧离子包围成配位立方八面体，配位数为12；钙离子位于立方晶胞的角顶，为6个氧离子包围成配位八面体，配位数为6，这是一个高度灵活变化的结构，在它的十四面体和八面体结构中的位置上，元素周期表中几乎每一种元素都能被容纳。理想的立方钙钛矿的结构就好像是一个三维数组的八面体BO6被连起来的顶点和被8 BO6包围的十四面体空腔中的离子。通常来说，由稀土或碱土离子占据A位置,但一个较小的离子,像一个镧系元素,也可以安排在这个位置。然而如果离子太小就会发生一些扭曲。