摘要近几年，纳米多孔材料以其优良的物理化学性能、独特的双连续结构特征，更高的比表面积，吸引了大批研究者的注意，得到了极大程度的发展，它可以用于催化，分离等多种应用领域，使得多孔材料的体系有了新的突破方向。本文采用去合金化法的方法对非晶前驱体Ti40。6Zr9。4Cu40。6Ni6。3Sn3。1进行纳米多孔铜材料的制备。实验分别在40℃，60℃和75℃以及0。1MHF溶液和0。2MHF溶液中完成，实验时间为2h到12h，梯度为2h。通过控制变量的方法对比后发现，去合金化时间越长，温度越高，材料所得到的孔径尺寸越大，韧带尺寸也越大。此外，溶液HF的浓度对孔径尺寸和韧带尺寸的影响也呈正性的相关。同时EDS数据也显示，与前驱体相比较，随着去合金温度、去合金化时间和溶液浓度的增加，Cu元素的比例大幅度增加，其他元素如O和Ni、Sn等的比例相应的逐步在降低。因此我们得到结论：去合金温度和去合金化时间以及溶液浓度的增加对纳米多孔材料的形成都是有利的。81140

毕业论文关键词：去合金化  纳米多孔铜  腐蚀行为  孔径尺寸

毕业设计说明书外文摘要

Title  Fabrication and the micro-structure of the nano-porous material through dealloying amorphous alloy

Abstract In recent years, nano-porous material’s excellent physical, bicontinuous structure, higher specific surface area and chemical properties attracts attention of a large number of researchers, which achieve great improvement of it。 Nano-porous material can be used in the field of catalysis, separation and provide new breakthrough to the system of porous material。 This thesis uses the methods of dealloying to product the nano-porous copper through the amorphous precursor Ti40。6Zr9。4Cu40。6Ni6。3Sn3。1。 The experiments are proceeded in an temperature environment of 40℃,60℃ and 75℃, and also the concentration environment of 0。1M HF solution and 0。2M HF solution respectively。 The time of the experiments is 2h to 12h, with the gradient of 2h。 After comparing we found that the longer the etching time, the bigger pore size  and ligament size we can get。 Besides, concentration of the HF solution also has the positive correlation with the pore size and ligament size。 Meanwhile, the data of EDS also show that compared with the precursor, along with the increase of temperature, etching time and solution concentration, element of Cu are rising in a significant speed and also the proportion of the obstacle elements like O, Ni or Sn is reducing accordingly。 So we come to the conclusion that temperature, etching time and solution concentration can all increase the form of nano-porous material。 

Keywords  Dealloy    Nano-porous   Corrosion Behavior  Pore size

目   次

1  引言。。。。。。。 1

1。1  纳米多孔材料。1

1。1。1  纳米多孔材料的研究现状。。。。。。。。。。1

1。1。2  纳米多孔材料的制备方法。。。。。。1

1。2  去合金化法制备纳米多孔材料。2

1。2。1  去合金化制备法。。。。。。2

1。2。2  去合金化机理的研究进展。。。。。。3

1。2。3  去合金化制备法的优势。。4

1。3  非晶材料前驱体。。。。。4

1。4   本文研究内容。。。。。。。5

2  实验方法。。。。6

2。1  实验仪器。6

2。2  样品制备。6

2。3  反应原理。7

2。4  X射线衍射实验。。。。。。8

2。5  扫描电子显微镜。。。。。9

3  实验结果与分析。。。。。。11