highest, with an average of 1258。8℃。

(2)The order of the strength of the slag sample melting rate  is:  Alkalinity (CaO/SiO2) > Al2O3 > TiO2 > CaF2 > MgO >。 The Alkalinity (CaO /  SiO2)  have the greatest effect on the melting rate, the slag melting time in Alkalinity (CaO / SiO2) at 1。19 reaches its highest point, with an average of 20。7 minutes, the melting rate is the slowest;

the slag melting time in Alkalinity (CaO / SiO2) at 1。50 dropped to the lowest point, the average was 5。8 minutes for, then melting speed most quickly。 The MgO content in slag melting speed minimum when the MgO content (%) in between 6% to 10%, slag melting time increase with the content of MgO (%) decreased, in the 10% down to the lowest point in。 At this time the slag melting speed most quickly。

(3)The optimal ratio of slag system is: Alkalinity (CaO/SiO2):1。33; Al2O3 content: 6%; CaF2 content: 8%; MgO content: 9。5%; TiO2  content: 5%。

Key words: Titanium alloy; Melting point; Melting rate; Refining slag system

目 录

第一章 绪论 1

1。1 概述 1

1。2 钛合金冶炼技术 1

1。2。1 真空自耗电弧炉熔炼法 1

1。2。2 钛合金炉外精炼法 3

1。3 国内外含钛渣研究现状 4

1。3。1 国内含钛渣研究现状 4

1。3。2 国外含钛渣研究现状 5

1。3。3 含钛渣炉外精炼法研究背景 5

1。4 本课题研究的主要内容及意义 5

1。4。1 本课题研究的意义 6

1。4。2 本课题研究的主要内容 6

第二章 试验研究方法及设备 7

2。1 精炼渣的性质 7

2。2 试验精炼渣的组成设计 7

2。2。1 渣系选择 7

2。2。2 渣系组成 10

2。3 试验设备及操作 10

第三章 试验结果与数据分析 14

3。1 各组分对于渣系熔化温度的影响 14

3。2 各组分对于渣系熔化速度的影响 20

结 论 25

致 谢 26

参考文献 27

第一章 绪论

1。1 概述

随着社会的发展和科学技术的进步以及各种新产业、新技术的出现，人们对于生 产材料质量的要求越来越高。传统的钢、铜、铝等合金本身的不足也越来越明显，在 这种情况下，钛及钛合金的研究、生产及应用也就显得越来越重要。

钛及钛合金具有许多优异的物理化学特性，例如熔点高、无磁性、热膨胀系数低、 比强度（强度/密度)和比刚度（弹性模量/密度)高以及耐腐蚀性能好、耐生物侵蚀等， 因此钛及钛合金材料成为航空、航天飞行器等高技术领域至关重要的关键结构材料。 与此同时钛及钛合金材料在能源、化工、石油、舰船、生物医学等民用领域也得到了 越来越多的应用。钛及钛合金材料技术研究往往被分为军用与民用或者是航空与非航 空两大领域，它们各有不同的发展趋势。航空领域主要考虑的是材料的力学性能如比 强度、比刚度和耐热性、韧性、疲劳寿命等，综合力学性能最优的钛合金为最佳选择； 而非航空领域则将腐蚀性、加工性和成本等作为主要考虑的因素，在此领域中，以工 业纯钛、成分较简单或者是低合金化的通用钛合金为主要选择[1]。