钢渣尾矿中硅酸盐相的溶解行为研究
研究了水杨酸溶液对钢渣尾矿中硅酸盐相的萃取。实验分为三个方面，第一个是溶解时间对溶解量的影响；第二是水杨酸的浓度对溶解量的影响；第三个是不同的比表面积对溶解量的影响。通过研究发现，SAM溶液萃取硅酸盐相可以取得很好的效果，通过测定水杨酸萃取硅酸盐的含量，可以很快速的评价钢渣的胶凝活性。将比表面积为5克的钢渣放入0。2g/ml水杨酸溶液中反应三个小时后，发现钢渣中硅酸盐几乎被完全反应而其他的矿物却反应很少。实验研究表明，水杨酸产生的阴离子和硅酸盐产生的阳离子产生的络合物削弱了氧化硅的稳定性。
毕业论文 关键词：硅酸盐；萃取；钢渣尾矿；水杨酸
Abstract With the rapid development of the steel industry, every year a large number of steel slag is discharged。 Thus not only caused a lot of waste non- renewable resources, but also seriously polluted the environment。 Therefore, the rational use of steel slag comprehensive utilization will become an urgent need。 But for now, primarily slag is used as a building material, in order to make the slag more fully and more reasonable use, focusing on the characteristics of the slag。
The main extraction of salicylic acid solution on the slag tailings silicate phase were pided into three parts, the first is the effect of the dissolution time of the experiment; the second is the effect of the concentration of salicylic acidexperiments; the third is the impact of different specific surface area of the experiment。 Through the study found, than the surface area of five grams of slag into the post 0。2g / ml solution of salicylic acid in the reaction of silicate slag was found three hours is almost completely reacted and other minerals but little reaction。 In laboratory studies it is one of the anion (HO-C6H4-COO-) and cations (Ca2 +) complexes generated undermine the stability of the silicon oxide。
Key words: silicate; extraction; slag
目 录
第一章 绪论 1
1。1钢渣的化学组成和形成过程 1
1。1。1钢渣的化学组成 1
1。1。2 钢渣的形成过程 2
1。3 钢渣的处理工艺 2
1。5 钢渣尾矿在国内外的研究现状 5
1。6 实验目的 9
1。7 研究内容 10
第二章 实验材料及方法 11
2。1 实验中用到的主要材料 11
2。2 实验仪器 11
2。2。1 实验的原料的制备 11
2。3 实验方法 11
2。3。1 不同的有机酸对钢渣溶解量的影响 12
2。3。2 水杨酸溶解不同粒度的钢渣 12
2。3。3不同的溶解时间 13
2。3。3不同的溶液浓度 14
第三章 水杨酸萃取其中硅酸盐相的溶解行为的研究 16
3。1有机酸对钢渣溶解量的影响 16
3。2。1 钢渣粒度对钢渣溶解量的影响 16
3。2。2 溶解时间对钢渣溶解量的影响 17
3。2。3 水杨酸浓度对钢渣溶解量的影响 18
3。2。4钢渣溶解后的XRD分析 19
3。3。6 硅酸盐溶解量的计算 19
3。3。5 萃取机理 20