摘要：聚苯胺/石墨烯复合材料在电池和超级电容方面有着良好的潜在应用价值。本文在综述石墨烯和聚苯胺的基础上，采用了低温酸性条件下聚苯胺混合溶液浸泡石墨烯的方法制得了二者的复合材料，分别利用扫描电镜和 X-射线衍射仪对合成的材料进行了形貌表征和结构分析，并测试了电容性能，得到了聚苯胺量越多，合成复合材料的电容性能越差的结论。该实验进一步阐述了石墨烯和聚苯胺的性质，探究了二者合成材料的电化学性能。85720

毕业论文关键词：聚苯胺，石墨烯，复合材料，电化学性能

Abstract：Polyaniline-graphene composites has a good potential for battery and supercapacitor applications。 In this paper, based on the synthesis of graphene and polyaniline, the composite materials was prepared by impregnating the graphene with polyaniline mixed solution under low temperature acid condition。 The morphologies and structures of the composites was characterized by scanning electron microscopy and X-ray diffractometer, and tested the capacitance performance。 It is concluded that the higher the amount of polyaniline, the worse the capacitance of the composite。 The properties of graphene and polyaniline was further elucidated, and the electrochemical properties of the composites was investigated。

Keywords: Polyaniline, Graphene, Composites, Electrochemical properties

目  录

1 前言 4

1。1 石墨烯概述 4

1。1。1 石墨烯的结构与特性 5

1。1。2 石墨烯的制备方法源Q于W优H尔J论K文M网WwW.youeRw.com 原文+QQ75201.,8766 与应用现状 7

1。2 聚苯胺概述 8

1。2。1 聚苯胺的结构与特性 8

1。2。2 聚苯胺的制备方法与应用现状 9

1。3 聚苯胺/石墨烯复合材料 10

2 试剂、设备与过程 11

2。1 原料与试剂 11

2。2 主要仪器设备 11

2。3 实验过程 12

3 测试与表征 12

3。1 扫描电子显微镜测试分析 12

3。2 X-射线衍射仪测试分析 12

3。3 恒电流充放电测试电容性能 13

4 结果与讨论 13

4。1 聚苯胺/石墨烯复合材料的表征 13

4。2 聚苯胺/石墨烯复合材料的X-射线衍射分析 15

4。3 聚苯胺/石墨烯复合材料的电容性能 16

小  结 18

参考文献 19

致谢 20

1 前言

自工业以来，全球化和工业化不断发展，在极大地改善了人类生活质量的同时，快速的发展也带来了一系列问题，能源匮乏和环境污染是最为突出的两个方面。工业的传统能源来自化石能源，这种能源不仅不可再生，并且由于人类不合理的开发利用，导致了严重的环境污染，如空气污染、水污染和固体废弃物污染。随着全球工业化的进一步发展，化石能源的储存和供应越发捉襟见肘，为了人类的可持续发展大计，新型清洁能源的开发和储存成了当务之急。