Title Preparation and Performance of Colorless,Transparent Polyimide film Abstract Dianhydride 9FDA and diamine 2,2'-bis-trifluoromethyl -4,4'-diamino-diphenylether(TFODA) were adopted to prepare a colorless, transparent fluorinated polyimide (PI) film by two-step in N,N'-dimethylacetamide (DMAC).After the analysis of tensile strength, TG and Ultraviolet-visible spectrum, it is found that tensile strength of the resultant film reaches 85.0Mpa,T5% is larger than 530°C, T10% is over 550°C, cut-off wavelength is 330nm and transmission is up to 96.0%, which showed excellent comprehensive performance. We also investigated the influence of different content of 3,3’,4,4’-ODPA (n(9FDA):n(ODPA)= 9:1,8:2,7:3, 6:4,5:5 and 4:6 respectively ) on the mechanical property, thermal property and optical property compared with 9FDA- TFODA- PI. Results showed that the mechanical property and thermal property of PI films can be improved by adding ODPA, but the optical property and adhesion performance reduced. The incorporation of trifluoromethyl group into PI molecular chain can also decrease the adhesion performance of PI film with other materials significantly. By introducing silicon-containing diamine α-ω-diaminopropyl polysiloxanes (PMDS) into the molecular chain, we explored the effect of different silicon-containing diamine content (n(TFODA):n(PMDS)=95:5,90:10,85:15,80:20) on its various properties of PI film, especially on adhesion performance. It was found that when n(TFODA):n(PMDS)=90:10, adhesive force on glass plate of PI can achieve grade 2, boiling time is over 24 hours, tensile strength is 79.1Mpa,T5%=498℃, T10%=542℃, cut-off wavelength is 338nm and transmission is up to 93.7%, which presents excellent comprehensive performance.26053
- 上一篇：氟掺杂对纳米碳材料氧还原催化性能的影响研究
- 下一篇：呋喃并香豆素衍生物的合成
Keywords polyimide film; colorless and transparent; adhesive force.
Catalog
1 Introduction 1
1.1 Foreword 1
1.2 Overview of traditional polyimide 2
1.2.1 The development process of polyimide 2
1.2.2 The performance and application of polyimide 3
1.3 Overview of fluorinated polyimide 4
1.4 Overview of silicon containing polyimide 5
1.5 Colorless polyimide molecular design 5
1.5.1 Trifluoromethyl group introduced in PI chain 6
1.5.2 Introducing alicyclic structure in the main chain of PI 6
1.5.3 The introduction of large side groups in the PI chain 7
1.5.4 Other molecular design methods 8
1.6 Research objectives and content of this project 9
2 Preparation and Properties 9FDA-ODPA-TFODA- PI film 10
2.1 Experimental materials and equipment 10
2.1.1 Experimental materials 11
2.1.2 Experimental equipment 10
2.2 Experimental content 11
2.2.1 Drying of materials and equipment 11
2.2.2 Synthesis of PAA 11
2.2.3 Preparation of PI film by thermal imidization 12
2.3 Performance Testing 12
2.3.1 PI film mechanical property 12
2.3.2 PI film thermal performance test 12
2.3.3 PI film optical performance test 13
2.3.4 PI film adhesion test 13
-
单边季戊四醇修饰的Al-A...
-
Fe-Anderson型杂多酸的制备及条件优化
-
单边三羟甲基硝基甲烷修...
-
Tris-CH3修饰Ni-Anderson型杂多酸盐的合成研究
-
Co-Anderson型杂多酸的制备和优化
-
七年级英语教材的比较分...
-
单边三羟甲基乙烷修饰的...
高警觉工作人群的元情绪...
巴金《激流三部曲》高觉新的悲剧命运
浅析中国古代宗法制度
现代简约美式风格在室内家装中的运用
中国传统元素在游戏角色...
上市公司股权结构对经营绩效的影响研究
NFC协议物理层的软件实现+文献综述
C++最短路径算法研究和程序设计
江苏省某高中学生体质现状的调查研究
g-C3N4光催化剂的制备和光催化性能研究