摘 要：本课题利用淮安盱眙产凹凸棒土作为主要原料，通过调节并补充硅、铝元素的含量，应用水热合成法来制备分子筛。通过考察水钠比、凹凸棒土是否焙烧及铝酸钠溶液的制备和使用来寻求制备分子筛样品的最佳方案。通过对不同的分子筛成品分析，结果显示：当硅铝比为2:1，钠硅比为1。5:1，水钠比为50:1，并且加入新制的铝酸钠溶液时为最佳方案，通过表征分析发现样品的微晶形貌为球体结构，且分布比较均匀，综合其它分析手段可基本认定在该条件下制备的分子筛形态符合分子筛的基本特征。同时，通过对表征的结果分析也发现烘焙样品时要控制适宜温度，以防止晶体塌陷，产生结晶度较低现象。94566

毕业论文关 键 词：凹凸棒土，分子筛， 制备，表征 

Abstract: used the attapulgite mineral produced from Xuyi distriction, Huan’an city as the main material, a kind sample of molecular sieve has been prepared via hydrothermal synthesis method, which adjusted the content of silicon and aluminum,the ratio of sodium to water, the surface of attapulgite and the preparation and application of sodium aluminate solution and etc。 The results showed that the best sample could be prepared when the Si / Al ratio is 2:1, sodium silicon is 1。5:1, sodium and water ratio is 50:1, and adding sodium aluminate solution。 The results show that the microcrystalline morphology of the sample is spherical structure and the distribution is uniform。 Based on the other analysis methods, the molecular sieve morphology prepared under these conditions can meet the basic characteristics of the molecular sieve。 At the same time, through the analysis of the results of the results also found that baking samples to control the appropriate temperature to prevent crystal collapse, resulting in lower crystallinity。 

Keywords: attapulgite, molecular sieve, preparation, characterization

目 录

1课题意义 4

1。1 概述 4

1。2 分子筛的制备 6

1。3选题的意义 6

2 凹凸棒土的预处理 7

2。1  凹凸棒土的酸化 7

2。2改性后样品的分析及表征 7

3 凹土基分子筛的制备 10

3。1 主要原料及试剂 10

3。2 主要仪器 10

3。3 实验部分 11

4 产品分析及表征 12

4。1 BET分析 12

4。2 TG－差热分析 16

4。3 X射线衍射分析 19

4。4 SEM电镜扫描 20

结  论 22

参考文献 23

致  谢 25

1课题意义

1。1 概述

所谓分子筛，是一种硅铝酸盐化合物，该物质具有均匀的微孔结构，这些微孔能够实现对不同的物性组分进行分离，如饱和度和沸点有差异，或是大小不一的分子，即“筛分”。因为分子筛具有吸附性能高，热稳定性强的优点，使得分子筛在电子、天然气等工业中得到广泛运用。分子筛还可以作为催化剂或离子交换剂。一般的分子筛由硅、铝、氧三种元素组成，合成分子筛的原料大多是含有大量硅元素和铝元素的物质，例如硅胶、白炭黑等。但是由于环保因素及经济效益价值等原因，工业上大多采用天然矿物质为原料来合成分子筛，比如使用高岭土原位合成Na-Y型分子筛[1]。