摘  要：以盐酸羟胺为还原剂，采用一种简易的液相还原法合成出银纳米片。纳米片形貌主要有三角形、六边形以及相应的切角三角形和六边形。纳米片的宽度和厚度分别约为1 μm 和 50 nm。在液相还原体系中，引入适量表面活性剂PVP，可获得均一的银纳米颗粒。银纳米颗粒为准球形，粒径约为100 nm。采用DSC热分析方法研究了所获得的两种银纳米材料对高氯酸铵热分解的催化性能。研究发现：银纳米片和银纳米颗粒对高氯酸铵的热分解均具有优异的催化性能，可分别使高氯酸铵低温分解温度降低7 °C 和14 °C，高温分解温度降低60 °C和110 °C，表观分解热增加0。86 kJ·g–1和1。05 kJ·g–1。94652

毕业论文关键词：银纳米颗粒，银纳米片，形成机理，高氯酸铵

Abstract: An easy and effective method of silver nanoplate synthesis technique was created by reducing silver nitrate (AgNO3) with hydroxylamine hydrochloride (NH2OH·HCl) at room temperature。 Silver nanoplates of various shapes, including triangular, truncated triangular, hexagonal, and truncated hexagonal exhibited an average width and thickness of approximately 1 μm and 50 nm, respectively。 Silver nanoparticles were acquired by placing polyvinyl pyrrolidone (PVP) in the reaction solution。 The produced silver nanoparticles were quasi-spherical in shape and 100 nm in size。 The catalytic activity in the thermal decomposition of ammonium perchlorate (AP) was distinguished by DSC。 The outcomes revealed that the addition of silver nanoplates and nanoparticles diminished the low decomposition temperature of AP by 7 °C and 14 °C, led to a drop in the high decomposition temperature of AP by 60 °C and 110 °C, and led to a rise in the total DSC heat release by 0。86 and 1。05 kJ·g–1, respectively。

Keywords: Silver nanoparticle, Silver nanoplates, Formation mechanism, Ammonium perchlorate

目   录

1 引言 3

2 实验步骤 3

3 结果与讨论 4

3。1 银纳米片的形貌分析 4

3。2 银纳米颗粒的形貌分析 5

3。3银纳米片和纳米颗粒的XRD衍射图谱 5

3。4银纳米结构调控 6

3。5不同反应时间对产物形貌的影响 7

3。6不同反应时间对产物元素组成的影响 9

3。7银纳米片和纳米颗粒对高氯酸铵热分解的催化性能 9

结  论 11

参 考 文 献 12

致  谢 15

1 引言论文网

在宏观世界中，银通常比较稳定的存在，基本不溶于水，本身杀菌力及抗菌谱既没有那么强也没有那么广。但在纳米科学的微观世界中，纳米银技术是建立在量子化学、材料化学、生物化学三大基础学科上的产物，通过将银的材料尺度超细微化，使其达到纳米量级，充分利用它的表面效应、小尺寸效应和它反映出的不同于宏观世界银的各种新的特异性质和效应，可以实现其长效性、广谱性、抗菌性强、稳定性好，遇水功效更强的特点。由于纳米银其表面积大大增加，表面活性大大增强，因此显示出独特的热、电、光、声、磁、力学性能和催化性能，广泛应用到化工、医学、光学、电子、电器等行业，具有广阔的应用前景。