摘要本次试验通过对硼钛合金加热剂进行配方设计，并对配方中各物质的含量和粒度进行分析和多次对比试验，得出一种能在点火后0.5 s内达到1000 ℃高温的合金加热剂配方。在此配方的基础上，计算该配方加热剂的理论密度，在给定模具装药体积一定的情况下，通过不断的改变压药压力，从一开始的200 kg/cm2增加到750 kg/cm2，得到不同装药密度的药柱，利用热电偶测得不同情况下加热剂点火后产生的加热温度，并观察各次试验的最高温度以及持续时间，从而得到最佳压力下的加热剂配方。64338

毕业论文关键词  合金加热剂;  理论密度;  压药压力;   加热温度

毕业设计说明书（论文）外文摘要

Title   Research on a kind of alloy heating energetic materials              

Abstract The formula of the alloy heating agent was designed through the test and analysis in the content and particle size of each substance.And the designed alloy heating agent can reach 1000 degrees in 0.5 seconds.The theoretical density of the ally heating agent was calculated on the basis of the designed formula. Different temperature produced by the alloy agent was measured under different pressure from the range of 200 kg/cm2 and 750 kg/cm2. Then the optimum pressure was found by observing the maximum temperature and duration of each test.

Keywords  Alloy heating agent; Theoretical density; Charge pressure; Heating temperature

1  绪论 5

1．1  研究背景 5

1. 2  B和Ti反应的理论基础 5

1. 3  B和Ti反应的相关研究 6

1. 4  硼系延期药的相关研究 7

1. 5  铬酸钡的氧化剂特性 8

2  铬酸钡对比试验 9

2. 1  试验材料及仪器 9

2. 2  试验过程 9

2. 3  结果与讨论 10

3  不同压力探索试验 12

3. 1  试验材料及设备 12

3. 2  雷管探究试验 13

3. 2. 1  不同压力下雷管点火试验 13

3. 2. 2  试验结果与结论 16

3. 3  探究不同压力下反应放出的热量 17

3. 4  试验结果与结论 20

4  真空点火拓展试验 20

4. 1  试验材料及设备 20

4. 2  模具中混合药剂的压制 21

4. 3  真空点火试验过程 21

4. 4  试验结果和结论 23

结  论 24

致  谢 25

参考文献 26

1  绪论

1．1  研究背景

TiB2是一种高硬度、高熔点、高稳定性的耐磨材料。对于Ti与B粉体材料反应应用于含能材料领域的研究很少，国内外主要集中在通过磁控溅射等技术制备Ti和B复合薄膜应用于火工品点火桥领域。国内的中国工程物理研究院化工材料研究所等机构利用磁控溅射法交替沉积Ti和B制备多层含能薄膜[1]，单层厚度分别为230nm和250nm。对含能薄膜进行x射线衍射图谱测试，结果显示其成分为Ti和B单质状态，并采用高速运动记录系统记录含能薄膜点火过程，结果表明火花溅射距离可达到30mm左右。可以推断含能薄膜用于制作桥膜可提高火工品的点火能力。