摘要本实验研究的是用脉冲电镀的方法制备CoMoP催化剂,并对在制备CoMoP催化剂的过程的制备条件进行优化,在对所有的制备条件进行优化之后,制备出效率相对最高,产氢速率最快的催化剂。本催化剂使用的是海绵,以海绵为载体将金属元素镀在海绵上制备产氢催化剂。优化的条件有:电镀一中钴的浓度、硼酸的浓度、溶剂中EG的体积比例、镀液温度、电流密度、电镀时间的长短;浸渍液中钴的浓度、EG的体积比例、浸渍时间、浸渍温度;电镀二中次磷酸钠的摩尔浓度、氢氧化钠的浓度、钼酸钠的浓度、溶剂中EG的体积比例、镀液温度、镀二的电流密度及电镀时间;电镀一二的电镀波形也是重要的影响因素。并使用SEM、EDX方法对最优条件下的样品进行表征,发现样品电镀效果不错,放在产氢溶液产完氢之后,载体上的金属元素没有掉落。

该论文有图25幅,表3个,参考文献9篇。69106

毕业论文关键词:制备条件  CoMoP  脉冲电镀  催化剂性能  

The research and preparation of foam nickel hydrogen production performance of alcoholysis         supported cobalt catalysts

Abstract

This experimental research is CoMoP catalyst preparation from dc plating method, and the preparation process of CoMoP catalyst preparation conditions were optimized, after to optimize the preparation conditions for all, were relatively high efficiency, the fastest rate of hydrogen production catalysts. The catalyst using a sponge, sponge as a carrier for metal plating on the sponge preparation of catalyst for hydrogen production. Optimized conditions are as follows: the concentration of cobalt plating one, EG in the boric acid concentration, solvent volume ratio, temperature, current density and electroplating time length; In the pickling liquid cobalt concentration, the proportion of the volume of EG, dipping time, soaking time;Plating 2 molar concentration of sodium hypophosphite, sodium hydroxide concentration, concentration of sodium molybdate, EG in the solvent volume ratio, plating solution, plating temperature of the current density and electroplating time; The influence factors of plating or electroplating waveform is also important. And using  SEM, EDX methods for optimal conditions of samples were characterized, and found the sample plating effect is good, in after sodium borohydride solution to produce hydrogen, metal elements on the carrier didn't fall off.

The paper has a figure 25, table 3, 9 references.

Key Words:Preparation conditions  CoMoP  dc plating  catalyst performance

目  录

摘  要 I

Abstract II

图清单 IV

表清单 IV

1 绪论 1

1.1氢能 1

    1.2硼氢化钠制氢技术 2

    1.3金属催化剂 3

    1.4电镀 3

    1.5氢能源的应用与探究 4

2.实验 6

2.1实验材料及仪器 6

2.2 实验步骤 6

3 海绵制氢催化剂的性能研究 9

3.1 EDX分析 9

3.2 实验数据分析 10

4结论 17

4.1实验结果总结

上一篇:新型三维网状结构FeCoNi三元合金制氢催化剂电镀法制备及性能
下一篇:碳纤维负载CoPB制氢催化剂的制备

MoO3光催化剂制备及性能研究

以复合氧化物为载体的脱硝催化剂制备研究

g-C3N4/Ag3PO4复合光催化剂的...

掺氮多壁碳纳米管负载R...

加氢脱硫催化剂NiMo/AAC载体的改性

蜂窝状催化剂对脱硝性能的影响

g-C3N4光催化剂的制备和光催化性能研究

麦秸秆还田和沼液灌溉对...

我国风险投资的发展现状问题及对策分析

新課改下小學语文洧效阅...

LiMn1-xFexPO4正极材料合成及充放电性能研究

网络语言“XX体”研究

张洁小说《无字》中的女性意识

安康汉江网讯

ASP.net+sqlserver企业设备管理系统设计与开发

互联网教育”变革路径研究进展【7972字】

老年2型糖尿病患者运动疗...