摘要金属有机框架材料（Metal-Organic Frameworks，简称MOFs），是由金属离子或金属簇与有机配体通过自行组装或者相互连接而形成的一类具有周期性网络结构的晶态多孔框架材料。MOFs是一种有机-无机杂化材料，兼具无机材料和有机材料的优良特征，此特征使其在气体吸附、分离、催化等方面呈现出巨大的应用前景。本论文以帕莫酸为主配体，通过溶剂热的方法将其与过渡金属（Co2+、Ni2+、In3+）等自组装，合成具有一定孔道的金属有机框架材料；通过对反应条件的调试（包括温度、配体及金属盐的比例、溶剂的比例等）最终合成得到适用于X-射线单晶衍射数据收集的单晶，并通过红外光谱对其进行了基本的表征。69299

该论文有图7幅，表3个，参考文献13篇。

毕业论文关键词： 金属有机框架材料  单晶

Designs and Syntheses of Metal-Organic Frameworks Based on Pamoic Acid

Abstract

Metal-organic frameworks are kind of porous materials based on metal ions (or metal clusters) and organic ligands via self-assemble. Metal-organic frameworks can be applied in many fields such as gas storage, separation, and catalysis because they are inorganic-organic hybrid materials which process their fantastic properties. Herein, pamoic acid was employed to react with transition metal ions (including Co2+、Ni2+、In3+) to obtain some metal-organic frameworks. Some single crystals were obtained after changing the synthesis conditions (including the reaction temperatures, the ratios of ligands and metal ions and the ratios of solvents). They were good enough for the data collections by the X-ray diffraction detector, and were characterized by IR spectra. 

Key Words: metal-organic frameworks  single crystal

目  录

摘要-I

Abstract-II

目录III

图清单-IV

表清单-IV

1 绪论-1

1.1 MOFs材料的特点1

1.2应用及研究2

2 实验部分3

2.1实验仪器-3

2.2实验药品与溶剂3

2.3实验过程-3

3 结果与结论6

3.1红外谱图分析-6

4 结论9

参考文献10

致谢-12

图清单

图序号 图名称 页码

图1-1 帕莫酸的结构图 2

图3-1 PA的红外谱图 6

图3-2 实验条件优化前（左）、后（右）的红色晶体图片 7

图3-3 Co2+/In3+盐与PA合成的配合物的红外谱图

7

图3-4 实验条件优化前（左）、后（右）的绿色晶体图片 8

图3-5 Ni2+/In3+盐与配体PA合成的配合物的红外谱图

8

图3-6 红外谱图综合对比图 9

表清单

表序号 表名称 页码

表2-1 实验所需仪器 3

表2-2 药品及溶剂用量   5

表2-3 药品及溶剂用量