摘要：Cu2O是一种性质特殊的金属氧化物，在航空航海、农业、环保等领域广泛应用。本文运用水热法“一锅”合成不同形貌的氧化亚铜，考察还原剂、分散剂、温度对材料形貌的影响，并对材料进行了XRD、FE-SEM、TEM、XPS等表征。结果表明：70℃时以葡萄糖为还原剂合成了苦瓜状纳米棒和星形氧化亚铜，25℃下以抗坏血酸为还原剂合成立方体氧化亚铜，且当温度升高至45℃，其形貌变为具有锋利棱角的长方体；XRD和XPS结果表明合成的氧化亚铜晶形均一。该方法具有重复性好、操作简单与环保等优点。76068

毕业论文关键词：水热法，一锅，氧化亚铜，形貌，表征 

Abstract: Cuprous oxide is a kind of special metal oxides, which is important because of its application in various fields, such as the aviation and navigation, agriculture, environmental protection, etc。 In this paper, Cu2O materials with different morphologies were synthesized in one pot by hydrothermal method。 Effects of reductant, dispersant and temperature on material structures were studied。 The products were characterized by XRD, FE-SEM, TEM and XPS。 The results showed that novel ‘balsam pear’ rod and star shapes of Cu2O at 70℃ were obtained using glucose as a reducing agent。 The cubic shape of Cu2O was prepared at the reaction temperature of 25 ℃when using ascorbic acid as a reductant, but it changed into cuboid with sharp faces when the temperature was 45 ℃。 The results of XRD and XPS showed that uniform morphology of Cu2O was prepared。 The method is highly repeatable, simple and environment-friendly。

Keywords: hydrothermal method, one-pot, cuprous oxide, morphology, characterization 

目   录

1 前言 3

1。1氧化亚铜性质 3

1。2氧化亚铜形貌研究概况 4

1。3纳米氧化亚铜合成方法 4

1。3。1液相合成法 4

1。3。2 固相法 5

1。3。3气相法 5

1。3。4电化学法 5

1。3。5 高能射线辐射法 6

1。3。6 其他方法 6

1。4纳米氧化亚铜应用 10

1。4。1污水处理领域中的应用 10

1。4。2 防污涂料中的应用 11

1。4。3气体传感器中的应用 11

1。4。4太阳能电池中的应用 11

1。4。5农业中的应用 12

1。4。6其他应用 12

2 实验部分 12

2。1实验仪器 12

2。2实验药品 12

2。3实验过程 13

3 结果与讨论 13

3。1电镜分析 14

3。1。1 温度对产品影响 15

3。1。2 还原剂对产品影响 15

3。1。3 分散剂对产品影响 16

3。2 XRD分析 16

3。3 XPS 分析 16

结论