摘要：以草酸溶液和硝酸铈溶液为原料，利用超声辅助液相合成法，在表面活性剂聚乙烯吡咯烷酮（PVP)的帮助下, 合成具有类柳叶形貌的配位聚合物草酸铈纳米多级结构。获得的样品用X-射线粉末衍射（XRD)、红外(FT-IR)、热重(TGA)及N2吸附比表面测定（BET）进行了结构分析，测定了紫外(UV)和荧光性能。通过扫描电镜(SEM)研究, 分析了反应时间、PVP的用量对纳米多级结构的影响。并以类柳叶形貌草酸铈为前驱体，在空气中煅烧得到二氧化铈，并对所得二氧化铈的结构进行了表征。79621

毕业论文关键词：草酸铈、微纳米结构、超声法、二氧化铈

Abstract:  By reaction of cerous nitrate with oxalic acid in the presences of surfactant polyvinylpyrrolidone (PVP) at room temperature and by using ultrasonic auxiliary liquid phase synthesis method, cerium oxalate complex with pseudo willow leaf structure was obtained facilely。 The as-prepared sample was characterized by X-ray powder diffraction (XRD), infrared(FT-IR), thermogravimetric(TGA) and N2 adsorption and desorption isotherms measurement (BET)。 Followed by scanning electron microscopy (SEM) analysis, the influences of reaction time and the amount of PVP on hierarchical structure of cerium oxalate complex were investigated。 Moreover, by calcining cerium oxalate complex precursor in air, CeO2 was obtained, whose structure was also characterized。 

Keywords: cerium oxalate, micro/nano structure, ultrasonic method, cerium oxide

目   录

1 前言 5

2 实验部分 5

2。1 仪器 5

2。2 试剂 6

2。3 草酸铈的制备 6

2。3二氧化铈的制备 6

3 结果与讨论 6

3。1草酸铈的XRD分析 6

3。2草酸铈的FT-IR分析 7

3。3草酸铈的TGA分析 8

3。4草酸铈的UV的分析 9

3。5草酸铈的荧光分析 10

3。7草酸铈的SEM分析 11

3。7。1反应时间对类柳叶草酸铈结构的影响及形成机理 12

3。7。2表面活性剂PVP量对草酸铈结构的影响 13

3。8煅烧类柳叶草酸铈制得二氧化铈样品的分析 14

3。8。1二氧化铈的XRD的分析 14

3。8。2二氧化铈的BET的分析 14

3。8。3二氧化铈的SEM的分析 15

结   论 17

参 考 文 献 18

致  谢 19

1 前言

   纳米科学技术是20世纪80年代末期诞生并正在崛起的新兴科技，是以许多先进科学技术为基础的科学技术，它是现代科学和现代技术结合的产物。纳米材料的主要特点就是尺寸缩小，精度提高。纳米材料因其独特的表面效应、量子尺寸效应等而表现出不同于常规材料的特殊性能，因而在各个领域得到广泛的应用。近年来，人们对纳米材料的兴趣大大增加[1]。当组成材料的尺寸达到纳米量级时，纳米材料表现出的性质与体材料有很大的不同[2]。在纳米尺度范围内原子及分子的相互作用，强烈地影响物质的宏观性质[3]。