摘要：本实验是以三聚氰胺与甲醛溶液为原料，用氢氧化钠溶液调节其PH值为9，在35℃的条件下发生羟甲基反应生成预聚体；以盐酸调节体系的PH至为5，预聚物在在该条件下分散在石油醚中进行反向悬浮聚合，生成三聚氰胺甲醛树脂微粒。并对微粒进行红外光谱分析，结果表明生成的微粒为三聚氰胺甲醛树脂。这对提高三聚氰胺甲醛树脂的使用性是很有意义的。5895
- 上一篇：捣镐结构对使用寿命的影响+文献综述
- 下一篇：壁纸水性油墨的研制+文献综述
关键词： 离子交换，三聚氰胺，缩合反应，反向聚合，悬浮聚合，珠状
The Study of Methods for Prepare Melamine Resin
Abstract: The experiment is based on melamine and formaldehyde solution as raw material
and use Sodium hydroxide solution to adjust its PH value of 9. Then under the conditions at 35 ℃ which makes hydroxymethyl prepolymer reaction happen.Use Hydrochloric acid to adjust the PH of 5. In that condition prepolymer dispersed in petroleum ether, reverse suspension polymerization which generates Melamine-formaldehyde resin particles. IR spectrum of the fine particles shows that the generated particles are melamine formaldehyde resin which is meaningful to improve of the use of melamine-formaldehyde resin.
Key Words: Ion exchange；Melamine；Condensation reaction；Reverse polymerization；Suspension Polymerization；Beaded
目录
摘要 i
Abstract i
目录 ii
1 绪论 1
1.1 离子交换树脂的基本介绍 1
1.2 离子交换树脂的工作原理 1
1.2.1 晶格理论 2
1.2.2 双电层理论 3
1.2.3 Donnan膜理论 3
1.3 离子交换高分子树脂的制备 3
1.3.1 加成聚合 4
1.3.2 缩聚反应制备树脂 4
1.4 离子交换树脂的应用 5
1.5 本课题研究目的和内容 5
1.5.1 三聚氰胺与甲醛的摩尔比的影响 6
1.5.2 反应介质的pH 值的影响 6
1.5.3 反应温度的影响 6
2 试验部分 7
2.1 药品 7
2.2 仪器和设备 8
2.3 实验步骤 8
2.3.1 三聚氰胺树脂制备中原料配比的确定及计算 8
2.3.2 制取三聚氰胺预聚物即羟甲基三聚氰胺 9
2.3.3 聚甲基丙烯酸甲脂（PMMA）的制备 10
2.3.4 反向悬浮聚合阶段 11
2.4 性能测试：红外测试 12
3 结果与讨论 13
3.1 制取三聚氰胺预聚物的反应 13
3.1.1 实验现象及过程分析 13
3.1.2 反应过程及产物的分析 14
3.2 制取聚甲基丙烯酸甲脂（PMMA）的反应 14
3.2.1 实验现象分析 14
3.2.2 反应过程及产物的分析 14
3.3 羟甲基三聚氰胺的反向悬浮聚合反应 15
3.3.1 实验现象及过程分析 15
3.3.2 红外谱图分析 17
-
不同链长聚二甲基硅氧烷...
-
电弧离子镀TiAlN硬质薄膜的制备及性能研究
-
电弧离子镀TiCN硬质薄膜的制备及性能研究
-
稀土元素Dy对合金涂层结构与高温性能的影响
-
金属纳米晶体铁磁转变温度的热力学研究
-
热管/超声协同FSW弱连接的...
-
ZK60表面MAO-ED陶瓷/HA复合生物涂层的制备
C++最短路径算法研究和程序设计
巴金《激流三部曲》高觉新的悲剧命运
江苏省某高中学生体质现状的调查研究
NFC协议物理层的软件实现+文献综述
g-C3N4光催化剂的制备和光催化性能研究
高警觉工作人群的元情绪...
浅析中国古代宗法制度
中国传统元素在游戏角色...
现代简约美式风格在室内家装中的运用
上市公司股权结构对经营绩效的影响研究