摘要：本文在研究水性聚氨酯胶黏剂结构与性能的基础上，对其原材料比例、实验反应时间以及乳化剂转速对实验产品性能的影响。制备聚氨酯预聚体，在聚氨酯预聚体制备阶段添加DMPA；其次，制备水性聚氨酯乳液，为了提高水性聚氨酯的剥离强度及耐水、耐溶剂性能，分别以乙二胺为扩链剂、三乙胺为交联剂合成了水性聚氨酯胶黏剂。该制备方法简单，适合工业化生产，胶粘剂稳定性好、粘结力大、耐水性强、胶膜强度高。91761

毕业论文关键词： 水性聚氨酯 预聚体 胶粘剂

Abstract：This paper is based on the analysis of the structure and performance of Water-based polyurethane adhesive。DMPA is added to the preparation stage of polyurethane pre polymers; Secondly, the preparation of waterborne polyurethane emulsion, sterilization in order to improve the peel strength of waterborne polyurethane and water resistance, solvent resistance, the adhesive was synthesized by ethylene diamine and triethylamine as crosslinking agent。 The preparation method is simple, suitable for industrial production, the adhesive stability is good, the adhesive strength is large, the water resistance is strong, the film strength is high。

Key words：

目 录

第一章前言 4

第二章实验部分 6

2。1原料及仪器设备 6

2。1。1主要原料 6

2。1。2主要测试仪器及设备 6

2。2合成 7

2。2。1水性聚氨酯乳液（PU）的制备 7

2。2。2杀菌性水性聚氨酯的合成 7

2。3性能测试 7

2。3。1涂膜的制备 7

2。3。2涂膜吸水率的测定 7

2。3。3固含量的测定 7

2。3。4溶液的特征吸收峰的测定 8

2。3。5耐溶剂(丙酮)性能测试 8

2。3。6粘度的测定 9

2。3。7羟值的测定 9

第三章结果与论论 9

3。1反应时间对实验产品的影响 9

3。2原材料比例对实验产品的影响 9

3。3混合乳化剪切机的转速对实验产品的影响 10

结论 11

参考文献 12

致谢 13

1前言来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766

当前，随着我国国民经济的持续增长，人民健康的生活水平的持续提高，对胶黏剂的需求逐年增长。聚氨酯材料不仅具有强度高、伸长度好、弹性大等特点，而且具有优异的耐磨性、耐油性、耐撕裂性、耐化学品性，减震性能好，硬度的调节范围大等优点，使其逐渐发展成为材料加工工业的重要材料。聚氨酯性能优异，极易加工成型，广泛用作于涂料、泡沫塑料、粘合剂等领域[1～3]。因为最先的水性聚氨酯是以有机溶剂做扩散剂，对环境和人体都有较大的伤害，所以开发新的环保型聚氨酯胶黏剂迫在眉睫。水性聚氨酯胶黏剂不仅可以和溶剂型胶黏剂的性能相媲美，而且具有无溶剂臭味、无污染、不可燃等其特有的优异性能。