摘 要：纤维板因化学胶黏剂的使用，导致其对环境污染较为严重，研究绿色无污染的纤维板就成为了目前研究的热点。本实验主要研究纤维素酶对秸秆预处理的工艺，以期为绿色无胶纤维板研制提供依据。首先对纤维素酶预处理工艺的单因子进行了优化，优化条件为：酶量为1。25U/g，时间为4h，温度50℃，固液比1:3，pH4。4；进一步进行了SAS响应面优化，优化结果为：酶量1。25U/g，反应时间3h，温度45℃，固液比1:3，pH4。4。在该条件下，研制的纤维板弯曲强度达到6。20MPa,与未优化相比提高了1。17倍。本实验为纤维素酶处理秸秆纤维制备力学性能优良的自生胶合纤维板提供了理论依据。92659

毕业论文关键词：纤维板，纤维素酶，小麦秸秆，预处理，弯曲强度

Abstract:Environmental pollution is more serious because of the use of chemical adhesives of fiberboard,research on green non-pollution fiberboard has become a hotspot。This paper is the research on cellulose treatment of straw, in order to provide the basis for development of green fiberboard 。 First process of the cellulose treatment is optimized by single factor。 Optimum conditions:enzyme amount 1。25U/g,reaction time 4h, treatment temperature 50℃,solid-to-liquid ratio 1:3, pH 4。5; further for the SAS response surface optimization, optimization results: enzyme amount 1。25U / g, reaction time 3h, solid-liquid ratio 1:3, pH4。4,treatment temperature 45℃。In this condition, the flexural strength of fiber board are respectively reached 6。20MPa,。It increaseded 1。17 times compared with not optimized。The research provided the theoretical guidance for production of self-bonding straw fiberboard with excellent performance。

Keywords:fiberboard, cellulose, wheat straw, pretreatment, flexural strength

目   录

1 前言 1

1。1 我国人造板发展现状 1

1。2 纤维板的研究进展 2

1。2。1 纤维板生产现状 2

1。2。2 环保型生产工艺 3

1。3 纤维素酶预处理生产无胶纤维板 3

1。4 研究思路 4

2 材料与方法 5

2。1 材料与仪器 5

2。1。1 秸秆 5

2。1。2 试剂 5

2。1。3 溶液 5

2。1。4 仪器设备 5

2。2 实验方案 6

2。2。1 纤维素酶预处理秸秆的单因素条件研究 6

2。2。2 纤维板响应面优化 6

2。2。3 纤维板热压方法 7

2。2。4 力学强度测定 7

3 结果与分析 8

3。1 不同酶量对纤维板性能的影响 8

3。2 不同时间对纤维板性能的影响 8

3。3 不同固液比对纤维板性能的影响 9

3。4 不同pH对纤维板性能的影响 10

3。5 不同温度对纤维板性能的影响 10

3。6 响应面优化及验证性实验分析 11

4 结论与展望