摘要： 本文以β-CD为原料，环氧氯丙烷(ECH)为交联剂制备环糊精聚合物，通过改变不同的进料比，探讨环氧氯丙烷与环糊精的配比对其产物溶解性的影响，然后用巯基环糊精代替环糊精制备巯基环糊精聚合物，并利用红外（FTIR）和核磁光谱对所得产物进行表征。结果表明，环氧氯丙烷与环糊精的配比进料比低于35:1（ECH：β-CD）时，聚合物为水溶性，进料比高于35:1（ECH：β-CD）时，聚合物为非水溶性。10540
- 上一篇：儿童自闭症及其社工介入问题研究
- 下一篇：辛伐他汀的含氟修饰物研究
关键词： 环糊精聚合物; 水溶性; 巯基环糊精; 配比
Synthesis and properties of cyclodextrin polymer
Abstract: In this thesis, the effect on solubility of cyclodextrin polymers, prepared by β-cyclodextrin (β-CD) and epichlorohydrin (ECH), has been discussed by changing the ratio between epichlorohydrin and cyclodextrin. In addition, thio- cyclodextrin polymer was also synthesized by using the thio-cyclodextrin and ECH. The structures of CD polymers were characterized by FT-IR and 1H NMR spectra. The results show that the ratio between epichlorohydrin and cyclodextrin is lower than 35:1, the CD polymers are water-soluble, and otherwise, the polymers are water-insoluble.
Keywords: Cyclodextrin polymer; water-solubility; thio-cyclodextrin; ratio
目录
1 绪论 1
1.1 课题研究的目的和意义 1
1.2 课题的研究背景 1
1.3 环糊精概述 2
1.4 环糊精聚合物的应用[9-13] 2
1.5 环糊精高聚物[16-19] 4
2 实验部分 5
2.1 仪器与试剂 5
2.1.1 仪器 5
2.1.2 药品与试剂 5
2.2 实验方法 5
2.2.1 6位单取代的-环糊精衍生物的制备 5
2.2.2 单巯基环糊精1的合成 6
2.2.3 β-环糊精聚合物2的制备 6
2.2.4 β-环糊精聚合物3的制备 6
2.2.5 β-环糊精聚合物4的制备 6
2.2.6 β-环糊精聚合物5的制备 6
2.2.7 β-环糊精聚合物6的制备 7
2.2.8 β-环糊精聚合物7的制备 7
2.2.9 用巯基环糊精代替环糊精制取β-环糊精聚合物8 7
3 结果与讨论 8
3.1 反应机理 8
3.2 反应条件 8
3.3 聚合物性质 9
3.3.1 ECH的用量与产物的水溶性分析 9
3.4 聚合物的表征 9
3.4.1 化合物1的谱图分析 10
3.4.2 聚合物2、3、4、5、6与β-环糊精的红外图谱分析 11
3.4.3 巯基环糊精聚合物的红外谱图分析 15
3.4.4 水溶性聚合物1、2、3的核磁图谱分析 16
3.4.5 巯基环糊精聚合物的核磁谱图分析 19
4 结论 20
致谢 21
参考文献 22
1 绪论
1.1 课题研究的目的和意义